PBT DURANEX® 2002 JAPAN POLYPLASTIC

344

Unit Price:US$ 3,820 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
52.1MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜Good flexibility｜Glass fiber reinforced｜Friction resistance
Application Areas:Electrical field｜Electronic field
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	190	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL 94	HB
UL flame retardant rating	UL flame retardant rating	0.710mm	UL 94	HB
Extreme Oxygen Index		ISO 4589-2	22	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ASTM D790/ISO 178	85	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	2540	kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	51	kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	>200	%
Impact strength of cantilever beam gap		ASTM D256/ISO 179	34	kg·cm/cm(J/M)ft·lb/in
Charpy Notched Impact Strength		ISO 179/1eA	3.2	kJ/m²
Bending modulus		ISO 178	3100	Mpa
bending strength		ISO 178	95	Mpa
tensile strength		ISO 527-1/-2	57	Mpa
bending strength		ISO 178	95.0	Mpa
Bending modulus		ISO 178	3100	Mpa
Nominal tensile fracture strain		ISO 527-2	12	%
tensile strength		ISO 527-2	57.0	Mpa
Bending modulus	23°C	ISO 178	2500	Mpa
bending strength	23°C	ISO 178	80.0	Mpa
bending strength	bending strength		ASTM D-790	85	Mpa
-40°C	-40℃	ASTM D638	3100	Mpa
23°C		ASTM D638	3170	Mpa
80°C	80℃	ASTM D638	469	Mpa
121°C	121℃	ASTM D638	296	Mpa
Surrender- 40°C		ASTM D638	101	Mpa
Yield, 0 ° C	Yield,0°C	ASTM D638	75.8	Mpa
Surrender, 23 ° C		ASTM D638	55.8	Mpa
Yield, 80 ° C		ASTM D638	24.8	Mpa
Yield, 121 ° C		ASTM D638	17.9	Mpa
yield		ISO 527-2/1A/50	60.0	Mpa
elongation		ASTM D-638	>200	%
Impact strength of cantilever beam gap		ASTM D-256	34	J/m
Bending modulus		ASTM D-790	2540	Mpa
tensile strength		ASTM D-638	51	Mpa
crack		ISO 527-2/1A/50	35.0	Mpa
50% strain	50%Strain	ISO 527-2/1A/50	30.0	Mpa
Surrender- 40°C		ASTM D638	7.2	%
Yield, 0 ° C	Yield,0°C	ASTM D638	4.4	%
Surrender, 23 ° C		ASTM D638	3.2	%
Yield, 80 ° C		ASTM D638	17	%
Yield, 121 ° C		ASTM D638	23	%
yield		ISO 527-2/1A/50	4.0	%
Fracture, 23 ° C		ASTM D638	200	%
crack		ISO 527-2/1A/50	220	%
Nominal tensile fracture strain		ISO 527-2/1A/50	>50	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	HDT	ASTM D648/ISO 75	70	℃（℉）
Linear coefficient of thermal expansion	TD：23to55°C	Internal Method	9E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23to55°C	Internal Method	9E-05	cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	80.0	°C
UL flame retardant rating		UL 94	HB
Hot deformation temperature	1.8Mpa	ISO 75-1/-2	80	°C
0.45MPa, unannealed		ASTM D648	160	°C
0.45MPa, unannealed	0.45MPa, unannealed		ISO 75-2/B	150	°C
1.8MPa, unannealed		ASTMD648	55.0	°C
Hot deformation temperature	1.82Mpa	ASTM D-648	70	°C
UL flame retardant rating		UL 94	HB
Glass transition temperature		ISO 11357-2	60.0	°C
Vicat softening temperature		ISO 306/B50	190	°C
Melting temperature		ISO 11357-3	225	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	1.1E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	1.4E-04	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792/ISO 1183	792
Water absorption rate	23°C,24hr	ISO 62	0.20	%
melt mass-flow rate		ASTM D1238	20	g/10min
Melt Volume Flow Rate (MVR)	250°C/2.16kg	ISO 1133	18.0	cm3/10min
flow		ASTM D955	1.8to2.0	%
Vertical flow direction		ISO 294-4	1.8to2.0	%
	Flow	ISO 294-4	1.8to2.0	%
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.19	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric strength	3.00mm	IEC 60243-1	17	KV/mm
Compared to the anti leakage trace index		IEC 60112	PLC 0
1MHz	1MHz	ASTM D150	3.20
100Hz	100Hz	IEC 60250	4.00
1MHz	1MHz	IEC 60250	3.50
Dissipation factor	100Hz	IEC 60250	1.4E-03
Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.022
Surface resistivity		IEC 60093	1E+15	ohms
--1		ASTM D149	17	KV/mm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Scale	ISO 2039-2	85
Rockwell hardness	Rockwell hardness	M-Sale	ISO 2039-2	78
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
ColourNumber			EF2001/ED3002

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.