POM LNP™ LUBRICOMP™ KL-4540 SABIC INNOVATIVE US
226
- Unit Price:US$ 4,798 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:38.5MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Low extract｜Internal lubrication
- Application Areas:Medical and nursing supplies｜Electrical appliances｜Plastic bag
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8 MPa, 未Annealed, 3.20 mm | ASTM D648 | 87.0 °C |
| 1.8 MPa, 未Annealed, 4.00 mm, 64.0 mm 跨距6 | ISO 75-2/Af | 79.0 °C | |
| Linear coefficient of thermal expansion | 流动 : -40 to 40°C | ASTM E831 | 1.1E-4 cm/cm/°C |
| Across Flow : -40 到 40°C | ASTM E831 | 1.1E-4 cm/cm/°C |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | 流动 : 24hr | ASTM D955 | 2.1 - 2.9 % |
| Across Flow流动 : 24小时 | ASTM D955 | 2.1 - 2.9 % | |
| water absorption rate | 24 hr, 50% RH | ASTM D570 | 0.18 % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.43 % |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 80 °C | ||
| drying time | 4.0 hr | ||
| Temperature at the rear of the barrel | 175 to 190 °C | ||
| Temperature in the middle of the barrel | 195 to 205 °C | ||
| Temperature at the front of the material cylinder | 210 to 220 °C | ||
| Processing (melt) temperature | 200 to 215 °C | ||
| mold temperature | 80 to 110 °C | ||
| Back pressure | 0.200 to 0.300 Mpa | ||
| screw speed | 30 to 60 rpm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile modulus | --1 | ASTM D638 | 1830 Mpa |
| -- | ISO 527-2/1 | 2020 Mpa | |
| tensile strength | Yield2 | ASTM D638 | 43.0 Mpa |
| Yield | ISO 527-2/5 | 39.0 Mpa | |
| Break2 | ASTM D638 | 43.0 Mpa | |
| Break | ISO 527-2/5 | 39.0 Mpa | |
| elongation | Yield2 | ASTM D638 | 14 % |
| Yield | ISO 527-2/5 | 22 % | |
| Break2 | ASTM D638 | 30 % | |
| Break | ISO 527-2/5 | 43 % | |
| flexural modulus | 50.0 mm Span3 | ASTM D790 | 2020 Mpa |
| --4 | ISO 178 | 2080 Mpa | |
| bending strength | -- | ISO 178 | 60.0 Mpa |
| 断裂, 50.0 mm Span3 | ASTM D790 | 63.0 Mpa | |
| coefficient of friction | Dynamic | ASTM D3702 | 0.25 |
| Static | ASTM D3702 | 0.14 | |
| Wear factor | ASTM D3702 | 1.8E+6 10^-8 mm³/N·m |
| impact performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 620 J/m |
| 23°C6 | ISO 180/1U | 42 kJ/m² | |
| Dart impact | 23°C, Energy at Peak | ASTM D3763 | 3.00 J |
| -- | ISO 6603-2 | 1.00 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.