PC/ABS

PC/ABS Bayblend® T85 000000 COVESTRO GERMANY

256

Unit Price:US$ 3,019 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
21MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility｜High impact resistance
Application Areas:Electronic field｜Electrical field
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	-30°C	ISO 180	NoBreak
Impact strength of cantilever beam gap	23°C	ISO 180/A	48 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180/A	35 kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180	NoBreak

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.9mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile strain	Break,23°C	ISO 527-2/50	>50 %
Tensile strain	Tensile strain	Yield,23°C	ISO 527-2/50	4.7 %
tensile strength	Break,23°C	ISO 527-2/50	50.0 Mpa
tensile strength	tensile strength	Yield,23°C	ISO 527-2/50	54.0 Mpa
Tensile modulus	23°C	ISO 527-2/1	2300 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	8E-05 cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	126 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	107 °C
Vicat softening temperature	--	ISO 306/B50	128 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	130 °C
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	7.5E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
MeltViscosity	260°C	ISO 11443-A	250 Pa·s
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.20 %
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.70 %
Shrinkage rate	MD:260°C,3.00mm	ISO 2577	0.50-0.70 %
Shrinkage rate	Shrinkage rate	TD:260°C,3.00mm	ISO 2577	0.50-0.70 %
Melt Volume Flow Rate (MVR)	260°C/5.0kg	ISO 1133	19.0 cm3/10min
density	23°C	ISO 1183	1.14 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 3
Dielectric strength	23°C,1.00mm	IEC 60243-1	35 KV/mm
Volume resistivity	23°C	IEC 60093	1E+16 ohms·cm
Surface resistivity		IEC 60093	1E+16 ohms
Dissipation factor	23°C,1MHz	IEC 60250	8.5E-03
Dissipation factor	Dissipation factor	23°C,100Hz	IEC 60250	2E-03
Relative permittivity	23°C,1MHz	IEC 60250	3.00
Relative permittivity	Relative permittivity	23°C,100Hz	IEC 60250	3.10

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC/ABS Bayblend® T85 000000 COVESTRO GERMANY

Material Description

Technical Data Sheet Compare

Technical Data Sheet