PA6 Ultramid®  8200HS BK102 BASF GERMANY

215
  • Unit Price:US$ 3,059 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    50MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Thermal stabilityhigh strengthOil resistant
  • Application Areas:Automotive ApplicationsEngine parts
  • Color:--
  • Grade:Injection grade

Material Certification

UL

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notch23°CISO 179NoBreak
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating3.0mmUL 94V-2
UL flame retardant rating6.0mmUL 94V-2
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulus23°CISO 527-22700 Mpa
tensile strengthYield,-40°CASTM D638136 Mpa
tensile strengthYield,23°CASTM D63885.0 Mpa
tensile strengthYield,121°CASTM D63823.0 Mpa
tensile strengthYield,-40°CISO 527-2136 Mpa
tensile strengthYield,23°CISO 527-280.0 Mpa
tensile strengthYield,120°CISO 527-223.0 Mpa
elongationYield,-40°CASTM D6383.0 %
elongationYield,23°CASTM D63820 %
Bending modulus65°CASTM D790460 Mpa
Bending modulus90°CASTM D790350 Mpa
Bending modulus121°CASTM D790305 Mpa
Bending modulus23°CISO 1782400 Mpa
bending strength-40°CASTM D790168 Mpa
bending strength23°CASTM D790110 Mpa
bending strength65°CASTM D79030.0 Mpa
bending strength90°CASTM D79020.0 Mpa
bending strength121°CASTM D79018.0 Mpa
bending strength23°CISO 17882.0 Mpa
elongationYield,121°CASTM D63815 %
Tensile strainYield,23°CISO 527-25.0 %
elongationBreak,-40°CASTM D6388.0 %
elongationBreak,23°CASTM D63860 %
elongationBreak,121°CASTM D638>100 %
Nominal tensile fracture strain-40°CISO 527-28.0 %
Nominal tensile fracture strain23°CISO 527-225 %
Nominal tensile fracture strain120°CISO 527-2>100 %
Bending modulus-40°CASTM D7903010 Mpa
Bending modulus23°CASTM D7902830 Mpa
thermal performanceTest ConditionTest MethodTest Result
Melting temperatureISO 3146220 °C
Linear coefficient of thermal expansionMDASTME8318.3E-05 cm/cm/°C
RTI Elec0.71mmUL 746130 °C
RTI Elec1.3mmUL 746130 °C
RTI Elec3.0mmUL 746130 °C
RTI Elec6.0mmUL 746130 °C
RTI Imp0.71mmUL 74695.0 °C
RTI Imp1.3mmUL 746105 °C
RTI Imp3.0mmUL 746105 °C
RTI Imp6.0mmUL 746105 °C
RTI Str0.71mmUL 74695.0 °C
RTI Str1.3mmUL 746105 °C
RTI Str3.0mmUL 746105 °C
RTI Str6.0mmUL 746105 °C
Hot deformation temperature0.45MPa,UnannealedASTM D648175 °C
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B150 °C
Hot deformation temperature1.8MPa,UnannealedASTM D64865.0 °C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A60.0 °C
Melting temperatureASTM D3418220 °C
Physical propertiesTest ConditionTest MethodTest Result
Water absorption rateEquilibrium,50%RHASTM D5702.7 %
Shrinkage rateMD:3.18mm1.2 %
Water absorption rate24hrASTM D5701.6 %
Water absorption rate23°C,24hrISO 621.6 %
Water absorption rateSaturationASTM D5709.5 %
Water absorption rateSaturation,23°CISO 629.5 %
Water absorption rateEquilibrium,23°C,50%RHISO 622.7 %
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessR-ScaleASTM D785119
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.