PFA TEFLON® 420HP DUPONT USA

572

Unit Price:US$ 30,430 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
13MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Blow molding grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	5.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	5.0	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	45	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	45	kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	7.0	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	8.0	kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	45	kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	45	kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	8.00	J
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Yield	ISO 527-2/5	125	Mpa
tensile strength	tensile strength	Yield	ASTM D638	120	Mpa
Tensile modulus		ISO 527-2/1	9300	Mpa
Tensile modulus	Tensile modulus		ASTM D638	9300	Mpa
Bending modulus	50.0mmSpan	ASTM D790	7580	Mpa
Bending modulus	Bending modulus		ISO 178	8500	Mpa
bending strength		ISO 178	195	Mpa
Tensile strain	Break	ISO 527-2/5	2.0	%
bending strength	Break,50.0mmSpan	ASTM D790	189	Mpa
tensile strength	Break	ASTM D638	120	Mpa
tensile strength	tensile strength	Break	ISO 527-2/5	125	Mpa
Tensile strain	Yield	ASTM D638	3.0	%
	Tensile strain	Yield	ISO 527-2/5	2.0	%
	Tensile strain	Tensile strain	Break	ASTM D638	3.0	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	2.5E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	2.5E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	1.2E-04	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	1.2E-04	cm/cm/°C
Vicat softening temperature	--	ISO 306/B120	215	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	215	°C
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	203	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	204	°C
Vicat softening temperature		ASTM D152514	215	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/A50	223	°C
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	220	°C
	Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	216	°C
	Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	217	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	TD：--5	Internal Method	0.60-0.90	%
	Shrinkage rate	MD：3.20mm	Internal Method	0.30-0.80	%
		Shrinkage rate	MD：--4	Internal Method	0.30-0.70	%
			Shrinkage rate	MD：--3	Internal Method	0.30-0.50	%
			Shrinkage rate	Shrinkage rate	MD：--2	Internal Method	0.50-0.80	%
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.080	%
	Water absorption rate	Saturation,23°C	ISO 62	0.26	%
	Water absorption rate	Water absorption rate	24hr	ASTM D570	0.060	%
Shrinkage rate	TD：3.20mm	Internal Method	0.50-1.0	%
	Shrinkage rate	TD：--4	Internal Method	0.50-1.0	%
	Shrinkage rate	Shrinkage rate	TD：--3	Internal Method	0.40-0.60	%
Melt Volume Flow Rate (MVR)	250°C/2.16kg	ISO 1133	13.0	cm3/10min
melt mass-flow rate	250°C/2.16kg	ASTM D1238	17	g/10min
Specific volume		ASTM D792	0.650	cm³/g
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		ASTM D257	>3.2E+16	ohms·cm
Dielectric strength	1.60mm,in Oil	ASTM D149	25	KV/mm
Dissipation factor	1MHz	ASTM D150	0.020
Dissipation factor	Dissipation factor	100Hz	ASTM D150	2E-03
Dielectric constant	1MHz	ASTM D150	3.70
Dielectric strength	3.20mm,inAir	ASTM D149	19	KV/mm
Dielectric constant	100Hz	ASTM D150	3.80
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	118
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
Filling material		ASTM D229	30	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Guangzhou HuShang Chemical	US$ 30420 /MT
Guangdong Huafu	US$ 59530 /MT

Supplier Join

Get App

Top

PFA TEFLON® 420HP DUPONT USA

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index