PBT VALOX™ 357XU-8269 SABIC INNOVATIVE US

154

Unit Price:US$ 3,174 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜UV resistance
Application Areas:Electrical appliances｜Plastic bag｜Casters｜Household goods｜Spool｜Shell｜switch
Color:--
Grade:--

Technical Data Sheet Compare

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R级	ASTM D785	117

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45MPa,未退火,3.20mm	ASTM D648	135 °C
	Heat Deflection Temperature	0.45MPa,未退火,6.40mm	ASTM D648	138 °C
		Heat Deflection Temperature	1.8MPa,未退火,3.20mm	ASTM D648	98.0 °C
			Heat Deflection Temperature	1.8MPa,未退火,6.40mm	ASTM D648	99.0 °C
			Heat Deflection Temperature	Heat Deflection Temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	84.0 °C
vicat		ASTM D152513	134 °C
	vicat	--	ISO 306/B50	145 °C
	vicat	vicat	--	ISO 306/B120	150 °C
ball-indentation hardness	125°C	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	9.2E-05 cm/cm/°C
	Linear coefficient of thermal expansion	MD：60to138°C	ASTME831	1.2E-04 cm/cm/°C
		Linear coefficient of thermal expansion	MD：-40到40°C	ISO 11359-2	7.2E-05 cm/cm/°C
			Linear coefficient of thermal expansion	TD：-40到40°C	ASTME831	8.4E-05 cm/cm/°C
			Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40到40°C	ISO 11359-2	8.4E-05 cm/cm/°C
RTI Elec		UL 746	120 °C
RTI Imp		UL 746	120 °C
RTI Str		UL 746	140 °C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.46mm	UL 94	HB
	UL flame retardant rating	0.63mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	5VA
Burning wire flammability index	1.0mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	1.0mm	IEC 60695-2-13	775 °C
	Hot filament ignition temperature	2.0mm	IEC 60695-2-13	750 °C
	Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC 60695-2-13	725 °C
Limiting Oxygen Index		ASTM D2863	30 %

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	45 kJ/m²
Impact strength of cantilever beam gap	-30°C	ASTM D256	150 J/m
	Impact strength of cantilever beam gap	23°C	ASTM D256	320 J/m
		Impact strength of cantilever beam gap	-30°C	ISO 180/1A	10 kJ/m²
			Impact strength of cantilever beam gap	23°C	ISO 180/1A	45 kJ/m²
			Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D4812	NoBreak
Dart impact	23°C,TotalEnergy	ASTM D3763	35.8 J
	Dart impact	23°C	ASTM D3029	43.4 J
	Dart impact	Dart impact	23°C11	ASTM D3029	43.0 J

Physical properties	Test Condition	Test Method	Test Result
shrinkage rate	MD：--2	内部方法	0.80-1.1 %
	shrinkage rate	MD：--3	内部方法	1.0-1.4 %
		shrinkage rate	MD：3.20mm	内部方法	1.0-1.4 %
		shrinkage rate	shrinkage rate	TD：--2	内部方法	0.90-1.3 %
Melt volume flow rate	250°C/5.0kg	ISO 1133	8.00 cm3/10min
density		ISO 1183	1.34 g/cm³
melt mass-flow rate	250°C/5.0kg	ASTM D1238	9.6 g/10min
Specific volume		ASTM D792	0.740 cm³/g
density		ASTM D792	1.35 g/cm³
shrinkage rate	TD：--3	内部方法	1.2-1.6 %
Water absorption rate	24hr	ASTM D570	0.080 %
	Water absorption rate	饱和,23°C	ISO 62	0.50 %
	Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ISO 62	0.15 %
Outdoor applicability		UL 746C	f2

Electrical performance	Test Condition	Test Method	Test Result
volume resistivity		ASTM D257	>1.2E+16 ohms·cm
dielectric strength	1.60mm,在油中	ASTM D149	25 KV/mm
	dielectric strength	3.20mm,inAir	ASTM D149	19 KV/mm
	dielectric strength	dielectric strength	3.20mm,在油中	ASTM D149	19 KV/mm
dielectric constant	100Hz	ASTM D150	3.20
dielectric constant	dielectric constant	1MHz	ASTM D150	3.20
Dissipation Factor	100Hz	ASTM D150	3E-03
Dissipation Factor	Dissipation Factor	1MHz	ASTM D150	0.030
arc resistance		ASTM D495	PLC6
Compared to the Leakage Tracking Index (CTI)	CTI	UL 746	PLC 2
High arc combustion index (HAI)	HAI	UL 746	PLC 3
High Voltage Arc Traceability Rate (HVTR)	HVTR	UL 746	PLC 3
Hot wire ignition (HWI)	HWI	UL 746	PLC 2

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Break	ASTM D638	42.0 Mpa
	tensile strength	屈服	ISO 527-2/50	50.0 Mpa
		tensile strength	屈服	ASTM D638	48.0 Mpa
		tensile strength	tensile strength	断裂	ISO 527-2/50	40.0 Mpa
Tensile strain	Yield	ASTM D638	5.0 %
	Tensile strain	屈服	ISO 527-2/50	5.0 %
		Tensile strain	Break	ASTM D638	54 %
		Tensile strain	Tensile strain	断裂	ISO 527-2/50	30 %
flexural modulus	50.0mm跨距	ASTM D790	2100 Mpa
flexural modulus	flexural modulus		ISO 178	2000 Mpa
bending strength		ISO 178	73.0 Mpa
	bending strength	屈服,50.0mm跨距	ASTM D790	78.0 Mpa
	bending strength	bending strength	Break,50.0mmSpan	ASTM D790	78.0 Mpa
Tensile modulus		ASTM D638	2020 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	2200 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.