Material Description
- Material Properties:High mobility｜Good liquidity｜Hydrolysis resistance｜Halogen-free｜Flame retardant｜Mineral reinforcement
- Application Areas:Fitness equipment｜Automotive Applications｜Thin walled products
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M 计秤 | ISO 2039-2 | 63 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 232 °C |
| 1.8 MPa, 未退火 | ISO 75-2/A | 185 °C | |
| 8.0 MPa, 未退火 | ISO 75-2/C | 103 °C | |
| vicat | ISO 306/A50 | 149 °C | |
| melting temperature | ISO 11357-3 | 280 °C | |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 0.0 cm/cm/°C |
| 横向 | ISO 11359-2 | 3.0E-5 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 100 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 130 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | 横向流量 | ISO 294-4 | 0.60 % |
| 流量 | ISO 294-4 | 0.0 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | > 1.0E+15 ohms | |
| volume resistivity | IEC 60093 | 1.0E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 40 KV/mm | |
| relative permittivity | 100 Hz | IEC 60250 | 3.80 |
| 1 MHz | IEC 60250 | 3.20 | |
| Dissipation Factor | 100 Hz | IEC 60250 | 0.010 |
| 1 MHz | IEC 60250 | 0.020 | |
| arc resistance | 内部方法 | 145 sec | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 150 °C | ||
| drying time | 4.0 to 6.0 hr | ||
| Suggested maximum moisture content | 0.010 % | ||
| Hopper temperature | 20 to 30 °C | ||
| Temperature at the rear of the barrel | 270 to 280 °C | ||
| Temperature in the middle of the barrel | 275 to 285 °C | ||
| Temperature at the front of the material cylinder | 280 to 290 °C | ||
| Spray nozzle temperature | 290 to 300 °C | ||
| Processing (melt) temperature | 285 to 295 °C | ||
| mold temperature | 80 to 120 °C | ||
| injection speed | 快速 | ||
| Back pressure | < 3.00 Mpa |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A | 10500 Mpa | |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 175 Mpa |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 4.5 % |
| flexural modulus | 23°C | ISO 178 | 11000 Mpa |
| bending strength | 23°C | ISO 178 | 175 Mpa |
| Compression Modulus | ISO 604 | 9500 Mpa | |
| compression stress | 1% 应变 | ISO 604 | 61.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.