PBT VALOX™ 4012G SABIC INNOVATIVE US

313

Unit Price:US$ 3,600 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
18MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Ductility｜Fast forming cycle
Application Areas:Laptop case
Color:--
Grade:Enhanced level

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	6.0	kJ/m²
	Impact strength of cantilever beam gap	23°C	ASTM D256	74	J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ASTM D256	74	J/m
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	45	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	45	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	7.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	6.0	kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	37	kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	37	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	6.0	kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	4.00	J
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.6mm	UL 94	HB
Burning wire flammability index	1.0mm	IEC 60695-2-12	750	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	Yield,50.0mmSpan	ASTM D790	110	Mpa
bending strength	bending strength		ISO 178	110	Mpa
Bending modulus		ISO 178	3500	Mpa
Tensile modulus		ASTM D638	4600	Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	4500	Mpa
tensile strength	Yield	ASTM D638	75.0	Mpa
	tensile strength	Yield	ISO 527-2/5	72.0	Mpa
		tensile strength	Break	ASTM D638	75.0	Mpa
		tensile strength	tensile strength	Break	ISO 527-2/5	72.0	Mpa
elongation	Yield	ASTM D638	3.0	%
Tensile strain	Yield	ISO 527-2/5	4.0	%
elongation	Break	ASTM D638	3.0	%
Tensile strain	Break	ISO 527-2/5	4.0	%
Bending modulus	50.0mmSpan	ASTM D790	3940	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed,100mmSpan	ISO 75-2/Be	215	°C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	175	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,100mmSpan	ISO 75-2/Ae	170	°C
Vicat softening temperature		ASTM D152511	205	°C
	Vicat softening temperature	--	ISO 306/B50	205	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	208	°C
Linear coefficient of thermal expansion	MD：23to80°C	ISO 11359-2	6E-05	cm/cm/°C
	Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	8E-05	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to150°C	ISO 11359-2	8.5E-05	cm/cm/°C
Ball Pressure Test	125°C	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	6E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to80°C	ISO 11359-2	8E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792	1.39	g/cm³
density	density		ISO 1183	1.39	g/cm³
melt mass-flow rate	250°C/1.2kg	ASTM D1238	10	g/10min
Melt Volume Flow Rate (MVR)	250°C/1.2kg	ISO 1133	9.00	cm3/10min
Shrinkage rate	MD：--2	Internal Method	0.60-0.90	%
Shrinkage rate	Shrinkage rate	MD：3.20mm	Internal Method	0.60-1.6	%
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.070	%
Shrinkage rate	TD2	Internal Method	0.70-1.0	%
Water absorption rate	Saturation,23°C	ISO 62	0.20	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dissipation factor	1MHz	IEC 60250	0.014
	Dissipation factor	60Hz	IEC 60250	1E-03
	Dissipation factor	Dissipation factor	50Hz	IEC 60250	1E-03
Relative permittivity	1MHz	IEC 60250	3.00
	Relative permittivity	60Hz	IEC 60250	3.10
	Relative permittivity	Relative permittivity	50Hz	IEC 60250	3.10
Dielectric strength	3.20mm,in Oil	IEC 60243-1	17	KV/mm
Dielectric strength	Dielectric strength	1.60mm,in Oil	IEC 60243-1	25	KV/mm
Surface resistivity		IEC 60093	>1.0E+15	ohms
Volume resistivity		IEC 60093	>1.0E+15	ohms·cm
Dielectric strength	0.800mm,in Oil	IEC 60243-1	30	KV/mm
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test	H358/30	ISO 2039-1	117	Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.