PA66 Ultramid® A3X3G5 BK BASF GERMANY
185
- Unit Price:US$ 4,010 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:52.6MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility｜heat-resisting
- Application Areas:Laptop case｜Industrial machinery
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | （23-80）℃，干态 | 2.5-3.5/6-8 10 | |
| Heat Deflection Temperature | 1.8MPa负荷，干态 | 250 °C | |
| maximum service temperature | 220 °C | ||
| Heat Deflection Temperature | 0.45MPa负荷，干态 | 250 °C | |
| TEMPERATURE | 在20000h/5000h，后拉伸强度下降50%时 | 135/153 °C | |
| specific heat | 干态 | 1.5 J/(g.K) | |
| thermal conductivity | 干态 | 0.27 W/(m.K) |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | 干/湿 | >10 Ω | |
| dielectric strength | K20/P50，干/湿 | 80/65 KV/mm | |
| Compared to the Leakage Traceability Index (CTI) | 干/湿 | CTI 600 M | |
| 干/湿 | CTI 500 | ||
| loss angle | 1MHz，干/湿 | 0.02/0.1 | |
| volume resistivity | 干/湿 | 10 Ω.cm | |
| dielectric constant | 1MHz，干/湿 | 3.7/5 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation | ≤0.5%, +23℃，湿 | 3500 Mpa | |
| Elongation at break | 干/湿，V=50mm/min | 3/4.5 % | |
| Tensile modulus | 干/湿 | 8500/6000 Mpa | |
| Charpy Notched Impact Strength | 30℃，干 | 65 KJ/m | |
| Impact strength of cantilever beam gap | +23℃，干/湿 | 11/17 KJ/m | |
| Tensile yield stress (V=50mm/min) | 干/湿 | 140/100 Mpa | |
| Elongation at break | 干/湿，V=50mm/min | 3/4.5 % | |
| Charpy Notched Impact Strength | +23℃，干/湿 | 70/75 KJ/m | |
| Tensile creep modulus | 1000h,湿 | 3500 Mpa | |
| Impact Strength | 干/湿 | 4/10 J | |
| Fracture stress (V=50mm/min) | 干/湿 | 140/100 Mpa | |
| Charpy Notched Impact Strength | +23℃，干/湿 | 13/18 KJ/m | |
| flexural modulus | 干/湿 | 7100 Mpa | |
| ball-indentation hardness | 干/湿 | 190 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.