PP Fibremod™ GB311U BOREALIS EUROPE

337

Unit Price:US$ 1,800 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜Detergent resistant｜filler｜Glass fiber reinforced material｜30%｜Filler by weight
Application Areas:Electrical appliances｜Electronic field｜Electrical field｜Application in the automotive field｜Electric｜Electronic application field｜component｜Home appliance components
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C,Injection	ISO 179/1eA	11 kJ/m²
Impact strength of simply supported beam without notch	-20°C,Injection	ISO 179/1eU	45 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C,Injection	ISO 179/1eU	50 kJ/m²
Impact strength of cantilever beam gap	-20°C,Injection	ISO 180/1A	8.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,Injection	ISO 180/1A	11 kJ/m²
Charpy Notched Impact Strength	-30°C,Injection	ISO 179/1eA	8.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-20°C,Injection	ISO 179/1eA	9.0 kJ/m²

flammability	Test Condition	Test Method	Test Result
Atomization	100°C	DIN 75201	1.0 mg

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	InjectionMolded	ISO 527-2/1	6800 Mpa
tensile strength	Yield,InjectionMolded	ISO 527-2	97.0 Mpa
Tensile strain	Break,InjectionMolded	ISO 527-2/50	3.0 %
Bending modulus	InjectionMolded	ISO 178	6200 Mpa
bending strength	InjectionMolded	ISO 178	130 Mpa

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature	--	ISO 306/B	135 °C
MeltEnergy		ISO 11357	75.7 kJ/kg
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	159 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	145 °C
Vicat softening temperature	--	ISO 306/A	165 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	230°C/2.16kg	ISO 1133	2.0 g/10min
Shrinkage rate	TD:2.00mm	Internal Method	1.0 %
Shrinkage rate	Shrinkage rate	MD:2.00mm	Internal Method	0.20 %
density		ISO 1183	1.12 g/cm³

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test	H132/10	ISO 2039-1	124 Mpa

Supplementary Information	Test Condition	Test Method	Test Result
Emission		VDA277	15.0 µg/g

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.