Material Properties:Easy electroplating
Application Areas:Electrical field｜Electronic field｜Fitness equipment｜Household appliances｜Household appliances｜Automotive sector
Color:--
Grade:Injection grade

Technical Data Sheet Compare

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	9E-05 cm/cm/°C
Heat Deflection Temperature	0.45MPa,未退火	ISO 75-2/B	112 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.8MPa,未退火	ISO 75-2/A	95.0 °C
vicat	--	ISO 306/B50	110 °C
vicat	vicat	--	ISO 306/B120	112 °C
Linear coefficient of thermal expansion	MD：23到55°C	ISO 11359-2	8.5E-05 cm/cm/°C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.9mm	UL 94	HB

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	-30°C	ISO 180/A	36 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/A	40 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180	NoBreak
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180	NoBreak

Electrical performance	Test Condition	Test Method	Test Result
Surface Resistivity		IEC 60093	1E+16 ohms
volume resistivity	23°C	IEC 60093	1E+16 ohms·cm
dielectric strength	23°C,1.00mm	IEC 60243-1	35 KV/mm
relative permittivity	23°C,100Hz	IEC 60250	3.10
relative permittivity	relative permittivity	23°C,1MHz	IEC 60250	3.00
Dissipation Factor	23°C,100Hz	IEC 60250	3.5E-03
Dissipation Factor	Dissipation Factor	23°C,1MHz	IEC 60250	8.5E-03
Compared to the Leakage Tracking Index (CTI)	解决方案A	IEC 60112	V

Physical properties	Test Condition	Test Method	Test Result
density	23°C	ISO 1183	1.10 g/cm³
Melt volume flow rate	260°C/5.0kg	ISO 1133	12.0 cm3/10min
shrinkage rate	TD:260°C,3.00mm	ISO 2577	0.55-0.75 %
shrinkage rate	shrinkage rate	MD:260°C,3.00mm	ISO 2577	0.55-0.75 %
Water absorption rate	饱和,23°C	ISO 62	0.70 %
Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ISO 62	0.20 %
MeltViscosity	260°C	ISO 11443-A	200 Pa·s

mechanical properties	Test Condition	Test Method	Test Result
Tensile strain	断裂,23°C	ISO 527-2/50	>50 %
Tensile modulus	23°C	ISO 527-2/1	2100 Mpa
tensile strength	屈服,23°C	ISO 527-2/50	49.0 Mpa
tensile strength	tensile strength	断裂,23°C	ISO 527-2/50	40.0 Mpa
Tensile strain	屈服,23°C	ISO 527-2/50	3.7 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.