Material Description

Material Properties:Flame retardant｜Oil resistant｜Halogen-free
Application Areas:Electrical applications｜Industrial machinery
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179	120	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	-40°C	ISO 527-2	8310	Mpa
Bending modulus	23°C	ASTM D790	5760	Mpa
Bending modulus	Bending modulus	-40°C	ASTM D790	5860	Mpa
Tensile strain	Break,23°C	ISO 527-2	10	%
elongation	Break,23°C	ASTM D638	10	%
tensile strength	Break,23°C	ISO 527-2	85.0	Mpa
tensile strength	tensile strength	Break,23°C	ASTM D638	90.0	Mpa
Tensile modulus	150°C	ISO 527-2	910	Mpa
	Tensile modulus	120°C	ISO 527-2	970	Mpa
		Tensile modulus	80°C	ISO 527-2	1360	Mpa
		Tensile modulus	Tensile modulus	23°C	ISO 527-2	6400	Mpa
Bending modulus	65°C	ASTM D790	1540	Mpa
	Bending modulus	90°C	ASTM D790	810	Mpa
		Bending modulus	121°C	ASTM D790	815	Mpa
		Bending modulus	Bending modulus	23°C	ISO 178	5200	Mpa
bending strength	-40°C	ASTM D790	207	Mpa
	bending strength	23°C	ASTM D790	138	Mpa
		bending strength	65°C	ASTM D790	55.0	Mpa
			bending strength	90°C	ASTM D790	35.0	Mpa
				bending strength	121°C	ASTM D790	34.0	Mpa
				bending strength	bending strength	23°C	ISO 178	140	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD		5.8E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD		4.6E-05	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ASTME831	5E-05	cm/cm/°C
Melting temperature		ISO 3146	220	°C
Melting temperature	Melting temperature		ASTM D3418	220	°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	195	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.6	%
	Water absorption rate	Equilibrium,50%RH	ASTM D570	1.6	%
		Water absorption rate	Saturation,23°C	ISO 62	5.7	%
			Water absorption rate	Saturation	ASTM D570	5.7	%
				Water absorption rate	23°C,24hr	ISO 62	1.1	%
				Water absorption rate	Water absorption rate	24hr	ASTM D570	1.1	%
Shrinkage rate	MD：3.18mm		0.90	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity	1.50mm	ASTM D257	>1.0E+15	ohms·cm
Volume resistivity	Volume resistivity		IEC 60093	>1.0E+15	ohms·cm
Dielectric strength	1.50mm	ASTM D149	22	KV/mm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	119
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C	Internal Method	6.78	J

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PA6 Ultramid® B3M8 BASF GERMANY

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index