PC/ABS LEXAN™ EXL1414-WH9A320 SABIC INNOVATIVE NANSHA
194
- Unit Price:US$ 5,315 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:50MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Easy to process｜Middle flow｜Good demolding performance｜copolymer
- Application Areas:Electronic field｜Electrical field
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.18 g/cm³ | |
| ISO 1183 | 1.19 g/cm³ | ||
| melt mass-flow rate | ASTM D1238 | 10 g/10 min | |
| Shrinkage rate | 内部方法 | 0.40 - 0.80 % | |
| 内部方法 | 0.40 - 0.80 % | ||
| Melt volume flow rate | ISO 1133 | 9.00 cm3/10min | |
| Water absorption rate | ISO 62 | 0.35 % | |
| ISO 62 | 0.15 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 89 | |
| ASTM D785 | 121 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Burning wire flammability index | IEC 60695-2-12 | 850 °C | |
| IEC 60695-2-12 | 960 °C | ||
| UL flame retardant rating | UL 94 | HB | |
| Hot filament ignition temperature | IEC 60695-2-13 | 875 °C | |
| IEC 60695-2-13 | 875 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2020 Mpa | |
| ISO 527-2/1 | 2150 Mpa | ||
| tensile strength | ASTM D638 | 55.0 Mpa | |
| ISO 527-2/50 | 57.0 Mpa | ||
| ASTM D638 | 50.0 Mpa | ||
| ISO 527-2/50 | 60.0 Mpa | ||
| elongation | ASTM D638 | 6.0 % | |
| ISO 527-2/50 | 6.0 % | ||
| ASTM D638 | 98 % | ||
| ISO 527-2/50 | 120 % | ||
| Flexural modulus | ASTM D790 | 2230 Mpa | |
| ISO 178 | 2250 Mpa | ||
| bending strength | ISO 178 | 85.0 Mpa | |
| ASTM D790 | 92.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 65 kJ/m² | |
| ISO 179/1eA | 70 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO 179/1eU | 无断裂 | |
| ISO 179/1eU | 无断裂 | ||
| Impact strength of cantilever beam gap | ASTM D256 | 770 J/m | |
| ASTM D256 | 870 J/m | ||
| ISO 180/1A | 60 kJ/m² | ||
| ISO 180/1A | 70 kJ/m² | ||
| Suspended wall beam without notch impact strength | ISO 180/1U | 无断裂 | |
| ISO 180/1U | 无断裂 | ||
| Dart impact | ASTM D3763 | 70.0 J |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| screw speed | 40 to 70 rpm | ||
| Exhaust hole depth | 0.025 to 0.076 mm | ||
| Spray nozzle temperature | 290 to 310 °C | ||
| Processing (melt) temperature | 295 to 315 °C | ||
| Temperature | 70 to 95 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| drying temperature | 120 °C | ||
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 40 to 60 % | ||
| Temperature in the middle of the barrel | 280 to 305 °C | ||
| Temperature at the rear of the barrel | 270 to 295 °C | ||
| Temperature at the front of the material cylinder | 295 to 315 °C |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | > 1.0E+15 ohms | |
| Volume resistivity | ASTM D257 | > 1.0E+15 ohms·cm | |
| dielectric strength | ASTM D149 | 16 KV/mm | |
| dielectric constant | ASTM D150 | 2.68 | |
| ASTM D150 | 2.64 | ||
| Dissipation Factor | ASTM D150 | 1.2E-3 | |
| ASTM D150 | 9.3E-3 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 139 °C | |
| ISO 75-2/Be | 140 °C | ||
| ASTM D648 | 124 °C | ||
| ISO 75-2/Ae | 128 °C | ||
| vicat | ASTM D152510 | 145 °C | |
| ISO 306/B120 | 146 °C | ||
| ball-indentation hardness | IEC 60695-10-2 | 通过 | |
| Linear coefficient of thermal expansion | ASTM E831 | 7.0E-5 cm/cm/°C | |
| ISO 11359-2 | 7.2E-5 cm/cm/°C | ||
| ASTM E831 | 7.5E-5 cm/cm/°C | ||
| ISO 11359-2 | 7.2E-5 cm/cm/°C | ||
| RTI Elec | UL 746 | 130 °C | |
| RTI Imp | UL 746 | 120 °C | |
| RTI | UL 746 | 125 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.