PC/PBT

PC/PBT XENOY™ HX6600HP 8H4D023 SABIC INNOVATIVE US

246

Unit Price:US$ 3,045 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
49MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility｜High impact resistance｜Dimensional stability
Application Areas:Automotive Applications
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	70 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	20 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	65 kJ/m²
Suspended wall beam without notch impact strength	-40°C	ISO 180/1U	NoBreak
Dart impact	23°C,TotalEnergy	ASTM D3763	100 J
Multi axis Instrumented Impact Energy		ISO 6603-2	100 J

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	1900 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	1900 Mpa
tensile strength	Yield	ASTM D638	43.0 Mpa
	tensile strength	Yield	ISO 527-2/50	44.0 Mpa
		tensile strength	Break	ASTM D638	35.0 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	37.0 Mpa
elongation	Yield	ASTM D638	4.0 %
Tensile strain	Yield	ISO 527-2/50	4.0 %
elongation	Break	ASTM D638	150 %
Tensile strain	Break	ISO 527-2/50	100 %
Bending modulus	50.0mmSpan	ASTM D790	1900 Mpa
Bending modulus	Bending modulus		ISO 178	1800 Mpa
bending strength		ISO 178	64.0 Mpa
bending strength	bending strength	Yield,50.0mmSpan	ASTM D790	43.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	95.0 °C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	60.0 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	60.0 °C
Vicat softening temperature		ASTM D152510	117 °C
	Vicat softening temperature	--	ISO 306/B50	117 °C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	120 °C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	1E-04 cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	1E-04 cm/cm/°C
		Linear coefficient of thermal expansion	MD：23to60°C	ISO 11359-2	1.3E-04 cm/cm/°C
			Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	1E-04 cm/cm/°C
			Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	1E-04 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	250°C/5.0kg	ASTM D1238	11 g/10min
Melt Volume Flow Rate (MVR)	250°C/5.0kg	ISO 1133	10.0 cm3/10min
Shrinkage rate	MD：3.20mm	Internal Method	1.2-1.6 %
Water absorption rate	Saturation,23°C	ISO 62	0.40 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.050 %
MeltViscosity	260°C,1500sec^-1	ISO 11443	210 Pa·s

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC/PBT XENOY™ HX6600HP 8H4D023 SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet