PP PRIME POLYPRO J705UG PRIME POLYMER JAPAN

304

Unit Price:US$ 1,371 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
22MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High rigidity｜Antistatic｜High impact resistance
Application Areas:--
Color:--
Grade:Wear resistant grade

Technical Data Sheet

other	Test Condition	Test Method	Test Result
characteristic			注塑高抗冲. 抗静电. 高刚性

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-20°C	ISO 179	4.0 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179	10 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	1450 Mpa
tensile strength	Yield	ISO 527-2	29.0 Mpa
Tensile strain	Break	ISO 527-2	50 %
Tensile modulus		ISO 527-2	1450 Mpa
Tensile stress	Yield	ISO 527-2	29 Mpa
Tensile strain	Break	ISO 527-2	50 %
Charpy Notched Impact Strength	-20℃	ISO 179	4.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23℃	ISO 179	10 kJ/m²
Rockwell hardness		ISO 2039-2	95
Impact strength of cantilever beam gap		ASTM D256/ISO 179	10 kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	50 %
Tensile modulus		ASTM D638/ISO 527	1450 kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	29 kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	95

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	105 °C
	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	105 °C
	Hot deformation temperature	Hot deformation temperature	HDT	ASTM D648/ISO 75	105 ℃（℉）

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	230°C/2.16kg	ISO 1133	9.0 g/10min
melt mass-flow rate	melt mass-flow rate	230℃,2.16kg	ISO 1133	9.0 g/10min
density		ASTM D792/ISO 1183	0.91
melt mass-flow rate		ASTM D1238/ISO 1133	9.0 g/10min

hardness	Test Condition	Test Method	Test Result
Rockwell hardness		ISO 2039-2	95

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PP PRIME POLYPRO J705UG PRIME POLYMER JAPAN

Material Description

Technical Data Sheet Compare

Technical Data Sheet