LCP VECTRA® A435-NC-VF3001 CELANESE USA

295

Unit Price:US$ 9,950 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜enhance｜Glass fiber reinforced
Application Areas:Automotive Applications｜Home appliance components
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	38	kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	33	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	23°C	ISO 178	206	Mpa
Compressive modulus		ISO 604	10500	Mpa
CompressiveStress	1%Strain	ISO 604	77.0	Mpa
Bending modulus	23°C	ISO 178	10500	Mpa
Tensile strain	Break	ISO 527-2/1A/5	3.3	%
tensile strength	Break	ISO 527-2/1A/5	171	Mpa
Tensile modulus		ISO 527-2/1A/1	11000	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD	ISO 11359-2	1.9E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	1E-06	cm/cm/°C
Melting temperature		ISO 11357-3	280	°C
Vicat softening temperature		ISO 306/B50	146	°C
Hot deformation temperature	8.0MPa,Unannealed	ISO 75-2/C	162	°C
	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	230	°C
	Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	250	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	2E-03	%
Shrinkage rate	MD	ISO 294-4	0.10	%
Shrinkage rate	Shrinkage rate	TD	ISO 294-4	0.40	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 60093	1E+15	ohms·cm
Surface resistivity		IEC 60093	>1.0E+15	ohms
Arc resistance		Internal Method	130	sec
Dissipation factor	1MHz	IEC 60250	0.016
Dissipation factor	Dissipation factor	100Hz	IEC 60250	0.020
Relative permittivity	1MHz	IEC 60250	3.10
Relative permittivity	Relative permittivity	100Hz	IEC 60250	3.50
Dielectric strength		IEC 60243-1	32	KV/mm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Scale	ISO 2039-2	55

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.