Material Description
- Material Properties:Flame retardant｜Glass fiber reinforced
- Application Areas:container｜Automotive sector
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8Mpa | 210 °C | |
| 0.45Mpa | 220 °C | ||
| UL flame retardant rating | V-0 | ||
| Heat Deflection Temperature | 1.8Mpa | 205 °C | |
| 0.45Mpa | 220 °C | ||
| UL flame retardant rating | HB | ||
| Heat Deflection Temperature | HDT | ASTM D648/ISO 75 | 205 ℃（℉） |
| HDT | ASTM D648/ISO 75 | 220 ℃（℉） | |
| melting temperature | 223 ℃（℉） | ||
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 40 mm/mm.℃ |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Limiting Oxygen Index | 30 % | ||
| 20 % |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting temperature | 223 °C | ||
| Water absorption rate | 空气中 | 0.2 % | |
| 水中 | 0.6 % | ||
| melting temperature | 223 °C | ||
| Water absorption rate | 空气中 | 0.15 % | |
| 水中 | 0.30 % | ||
| density | ASTM D792/ISO 1183 | 1.52 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.15 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric constant | 50Hz | 3.4 | |
| 1MHz | 3.4 | ||
| dielectric strength | 30 MV/m | ||
| dielectric constant | 50Hz | 3.3 | |
| 1MHz | 3.3 | ||
| arc resistance | 475 V | ||
| dielectric constant | ASTM D150/IEC 60250 | 3.3 | |
| arc resistance | ASTM D495/IEC 60112 | 475 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | 11000 Mpa | ||
| tensile strength | 140 Mpa | ||
| elongation | 断裂 | 2.5 % | |
| Impact strength of cantilever beam gap | 23℃ | 8.0 KJ/m | |
| -30℃ | 8.0 KJ/m | ||
| Tensile modulus | 10000 Mpa | ||
| tensile strength | 145 Mpa | ||
| elongation | 断裂 | 3.0 % | |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 10 kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 9 kg·cm/cm(J/M)ft·lb/in | ||
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 60 kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 70 kg·cm/cm(J/M)ft·lb/in | ||
| Tensile modulus | ASTM D638/ISO 527 | 10000 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 145 kg/cm²(MPa)[Lb/in²] | |
| Elongation at break | ASTM D638/ISO 527 | 3 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.