PA66 Amilan® CM3001-N/BK TORAY JAPAN

245

Unit Price:US$ 3,524 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
91MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant
Application Areas:Automotive sector｜Electrical components｜Electrical field｜Electronic field｜Electrical appliances
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-40°C	ISO 179	10 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179	13 kJ/m²
Impact strength of simply supported beam without notch	-40°C	ISO 179	60 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179	65 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.79 mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Taber abraser	1000 Cycles	ISO 9352	0.400 mg
Friction coefficient - vs. Metal		Suzuki Method	0.15
shear strength	23°C	ASTM D732	95.0 Mpa
Compressive stress	80°C	ISO 604	110 Mpa
	Compressive stress	23°C	ISO 604	180 Mpa
	Compressive stress	Compressive stress	-40°C	ISO 604	250 Mpa
bending strength	80°C	ISO 178	190 Mpa
	bending strength	23°C	ISO 178	290 Mpa
	bending strength	bending strength	-40°C	ISO 178	325 Mpa
Bending modulus	80°C	ISO 178	5800 Mpa
	Bending modulus	23°C	ISO 178	9500 Mpa
	Bending modulus	Bending modulus	-40°C	ISO 178	11600 Mpa
Tensile strain	Break, 80°C	ISO 527-2	5.0 %
	Tensile strain	Break, 23°C	ISO 527-2	2.5 %
	Tensile strain	Tensile strain	Break, -40°C	ISO 527-2	2.0 %
tensile strength	80°C	ISO 527-2	120 Mpa
	tensile strength	23°C	ISO 527-2	190 Mpa
	tensile strength	tensile strength	-40°C	ISO 527-2	235 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	262 °C
Melting temperature		DSC	265 °C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	2.0E-5 - 3.0E-5 cm/cm/°C
specific heat			1800 J/kg/°C
thermal conductivity			0.40 W/m/K

Physical properties	Test Condition	Test Method	Test Result
density	23°C	ISO 1183	1.37 g/cm³
Water absorption rate	Saturation, 23°C	ISO 62	5.5 %
Water absorption rate	Water absorption rate	24 hr, 23°C	ISO 62	0.60 %
Shrinkage rate	Flow : 3.00 mm	Internal Method	0.20 - 0.50 %
Shrinkage rate	Shrinkage rate	横向Flow : 3.00 mm	Internal Method	0.60 - 0.90 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		IEC 60093	1.0E+13 ohms·cm
Dielectric strength		IEC 60243-1	20 KV/mm
Dielectric constant	23°C, 50 Hz	IEC 60250	4.60
	Dielectric constant	23°C, 1 kHz	IEC 60250	4.40
	Dielectric constant	Dielectric constant	23°C, 1 MHz	IEC 60250	3.90
Dissipation factor	23°C, 50 Hz	IEC 60250	0.020
	Dissipation factor	23°C, 1 kHz	IEC 60250	0.020
	Dissipation factor	Dissipation factor	23°C, 1 MHz	IEC 60250	0.020
Arc resistance		UL 746	114 sec

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R -Sale, 23°C	ISO 2039-2	121
	Rockwell hardness	R -Sale, 80°C	ISO 2039-2	24
	Rockwell hardness	Rockwell hardness	M -Sale, 23°C	ISO 2039-2	97

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA66 Amilan® CM3001-N/BK TORAY JAPAN

Material Description

Technical Data Sheet Compare

Technical Data Sheet