PA66 Leona™ CR301 ASAHI JAPAN

427

Unit Price:US$ 4,110 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
67.3MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:dimensional stability ｜Conductive
Application Areas:Electrical components｜Electrical field｜Electronic field｜Switch panel｜Industrial applications
Color:--
Grade:Injection grade

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			电气特性
purpose			自动车电装部件
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch		ISO 179	51	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.75 mm	UL 94	HB
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	湿		1.5	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	干(湿)	ASTM D-256	34(39)	J/m
Rockwell hardness	干(湿)	ASTM D-785	85(-)	M Scale
flexural coefficient	干(湿)	ASTM D-790	5.9(2.9)	GPa
tensile strength	干(湿)	ASTM D-638	88(64)	Mpa
bending strength	干(湿)	ASTM D-790	147(93)	Mpa
Elongation at Break	干(湿)	ASTM D-638	3(3.5)	%
Rockwell hardness		ASTM D785	M85
Bending modulus		ASTM D790/ISO 178	5880(MPa)	kg·cm/cm(J/M)ft·lb/in
bending strength		ASTM D790/ISO 178	147(MPa)	kg·cm/cm(J/M)ft·lb/in
Taber abraser	1000 Cycles	ASTM D1044	--	mg
bending strength	23°C	ISO 178	140	Mpa
bending strength	bending strength	--	ASTM D790	147	Mpa
Bending modulus	23°C	ISO 178	7400	Mpa
Bending modulus	Bending modulus	--	ASTM D790	5900	Mpa
elongation	Break, 23°C	ISO 527-2	2.0	%
elongation	elongation	Break	ASTM D638	3.0	%
tensile strength	--	ASTM D638	88.0	Mpa
tensile strength	tensile strength	Break, 23°C	ISO 527-2	85.0	Mpa
Tensile modulus	23°C	ISO 527-2	7000	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	干	ASTM D-696	4	×10-5/K
Hot deformation temperature	1.82MPa,干	ASTM D-648	191(250)	°C
Combustibility (rate)		UL 94	HB
Hot deformation temperature	1.8 MPa, Unannealed	ASTM D648	191	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	188	°C
Linear coefficient of thermal expansion	Flow	ASTM D696	4.0E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		ASTM D696/ISO 11359	4	mm/mm.℃
Hot deformation temperature	HDT	ASTM D648/ISO 75	191	℃（℉）
	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	249	°C
	Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ASTM D648	250	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	干	旭化成方法	0.5-1.3	%
Wear factor	湿	ASTM D-1044	8	×10-6kg/1000times
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	--	%
Water absorption rate	Water absorption rate	Saturation, 23°C		--	%
Shrinkage rate	Flow	Internal Method	0.50 - 1.3	%
Water absorption rate		ASTM D570/ISO 62	1.5	%
Shrinkage rate		ASTM D955	0.5-1.3	%
density		ASTM D792/ISO 1183	1.48
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Arc resistance		ASTM D495/IEC 60112	150
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M -Sale	ISO 2039-2	85
Rockwell hardness	Rockwell hardness	M-Scale	ASTM D785	85

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PA66 Leona™ CR301 ASAHI JAPAN

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index