ABS

ABS POLYLAC® PA-705 ZHENJIANG CHIMEI

347

Unit Price:US$ 2,096 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details
Material Comparison:
ABS POLYLAC® PA-705 TAIWAN CHIMEI

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility｜High gloss
Application Areas:Lighting fixtures｜Casters｜Office supplies｜Automotive sector｜Electronic field｜Electrical field
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

other	Test Condition	Test Method	Test Result
characteristic			高刚性中冲击

Basic Performance	Test Condition	Test Method	Test Result
density	23℃	ASTM D-792	1.03
melt mass-flow rate	200℃，5kg	ASTM D-1238	2.7 g/10min

mechanical properties	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap		ASTM D256/ISO 179	20(3.7) kg·cm/cm(J/M)ft·lb/in
bending strength		ASTM D790/ISO 178	540（7.650） kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	1800（25500） kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	R-110
elongation		ASTM D638/ISO 527	35 %
tensile strength		ASTM D638/ISO 527	450（6.380） kg/cm²(MPa)[Lb/in²]
Impact strength of cantilever beam gap		ASTM D256/ISO 179	18(3.3) kg·cm/cm(J/M)ft·lb/in
bending strength	1/4"，2.8mm/min	ASTM D-790	680(9650) kg/cm2(lb/in2)
Bending modulus	1/4"，2.8mm/min	ASTM D-790	24000(340000) kg/cm2
Elongation at Break	1/8"，6mm/min	ASTM D-638	20 %
tensile strength	1/8"，6mm/min	ASTM D-638	450(6380) kg/cm2(lb/in2)
Impact strength of cantilever beam gap	1/4"，23℃	ASTM D-256	16(3.0) kg-cm/cm(ft-lb/in)
Rockwell hardness	1/2"	ASTM D-785	110 R scale

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature		ASTM D1525/ISO R306	104（219） ℃（℉）
Hot deformation temperature	HDT	ASTM D648/ISO 75	87（189） ℃（℉）
Hot deformation temperature	Hot deformation temperature	HDT	ASTM D648/ISO 75	98（208） ℃（℉）
Combustibility (rate)		UL 94	1/16"HB
Burning rate	1/16"	UL 94	HB
Hot deformation temperature	1/4"，50℃/hr	ASTM D-648	98(209) ℃（℉）
Vicat softening temperature	1/8"，50℃/hr	ASTM D-1525	104(219) ℃（℉）

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate		ASTM D1238/ISO 1133	27 g/10min
melt mass-flow rate	melt mass-flow rate		ASTM D1238/ISO 1133	2.7 g/10min
density		ASTM D792/ISO 1183	1.05

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

ABS POLYLAC® PA-705 ZHENJIANG CHIMEI

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet