PC/ABS Bayblend® FR3005-704013 COVESTRO SHANGHAI
168
- Unit Price:US$ 3,524 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜Chemical resistance
- Application Areas:Electrical field｜Electronic field｜Household appliances｜Household appliances｜Automotive sector
- Color:--
- Grade:--
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 90.0 °C |
| 1.8 MPa, 未退火 | ISO 75-2/A | 79.0 °C | |
| vicat | ISO 306/B120 | 96.0 °C | |
| Linear coefficient of thermal expansion | 流动 : 23 到 55°C | ISO 11359-2 | 7.1E-5 cm/cm/°C |
| 横向 : 23 到 55°C | ISO 11359-2 | 7.2E-5 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | V-0 |
| 1.8 mm | UL 94 | 5VB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | 无断裂 |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt viscosity | 240°C | ISO 11443-A | 120 Pa·s |
| ISO 9660 | PC+ABS-FR(40) |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | 240°C/5.0 kg | ISO 1133 | 38.0 cm3/10min |
| shrinkage rate | 横向流量 : 240°C, 3.00 mm | ISO 2577 | 0.30 - 0.50 % |
| 流量 : 240°C, 3.00 mm | ISO 2577 | 0.30 - 0.50 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1.0E+16 ohms | |
| volume resistivity | 23°C | IEC 60093 | 1.0E+17 ohms·cm |
| Compared to the Leakage Tracking Index (CTI) | 解决方案 A | IEC 60112 | PLC 2 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | 23°C | ISO 527-2/1 | 2700 Mpa |
| tensile strength | 屈服, 23°C | ISO 527-2/50 | 60.0 Mpa |
| 断裂, 23°C | ISO 527-2/50 | 45.0 Mpa | |
| Tensile strain | 屈服, 23°C | ISO 527-2/50 | 3.6 % |
| 断裂, 23°C | ISO 527-2/50 | > 40 % | |
| flexural modulus | 23°C | ISO 178 | 2800 Mpa |
| bending strength | 23°C | ISO 178 | 94.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.