ABS HU600SK KUMHO KOREA

264
  • Unit Price:US$ 3,095 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    10MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:heat-resisting
  • Application Areas:Electrical enclosure｜Automotive External Parts｜Parts under the hood of a car｜Application in the automotive field
  • Color:--
  • Grade:Heat resistant grade

Technical Data Sheet

otherTest ConditionTest MethodTest Result
characteristic超耐热、高耐冲击
purpose汽车配件、电器电子部件
Basic PerformanceTest ConditionTest MethodTest Result
melt mass-flow rate200℃/5kgASTM-D15251.8 g/10min
melt mass-flow rate220℃/10kgASTM-D12385.0 g/10min
density23℃ASTM-D7921.04
mechanical propertiesTest ConditionTest MethodTest Result
tensile strength23℃,50mmASTM-D63848 Mpa
elongation23℃,50mmASTM-D63815 %
bending strength23℃,3mmASTM-D79066 Mpa
Bending modulus23℃,3mmASTM-D7902254 Mpa
Rockwell hardnessASTM-D785108 R-Scale
Impact strength of cantilever beam gap3.2mm,Notched,23℃ASTM-D25619 kg.cm/cm
Impact strength of cantilever beam gap6.4mm,Notched,23℃ASTM-D25616 kg.cm/cm
Elongation at BreakASTM D638/ISO 52715 %
tensile strengthASTM D638/ISO 527490 kg/cm²(MPa)[Lb/in²]
Rockwell hardnessASTM D785108
Bending modulusASTM D790/ISO 17823000 kg/cm²(MPa)[Lb/in²]
bending strengthASTM D790/ISO 178670 kg/cm²(MPa)[Lb/in²]
Impact strength of cantilever beam gapASTM D256/ISO 17919 kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gapASTM D256/ISO 17916 kg·cm/cm(J/M)ft·lb/in
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature18.6kg/cm2,UnannealedASTM-D648100 °C
Vicat softening temperatureASTM-D1525110 °C
UL flame retardant rating1/8"UL 94HB
Combustibility (rate)UL 94HB
Hot deformation temperatureHDTASTM D648/ISO 75100 ℃（℉）
Vicat softening temperatureASTM D1525/ISO R306110 ℃（℉）
Physical propertiesTest ConditionTest MethodTest Result
Shrinkage rateASTM-D9550.4-0.7 %
densityASTM D792/ISO 11831.04
Shrinkage rateASTM D9550.4-0.7 %
melt mass-flow rateASTM D1238/ISO 11331.8 g/10min
melt mass-flow rateASTM D1238/ISO 11335.0 g/10min
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.