Material Description

Material Properties:High gloss
Application Areas:Electronic field｜Electrical field
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

other	Test Condition	Test Method	Test Result
purpose			冰箱把手及零组件
characteristic			耐HCFC.射出成型。

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ASTM D790	610 kg/cm2
Elongation at Break		ASTM D638	50 %
tensile strength	降伏点	ASTM D638	440 kg/cm2
Impact strength of cantilever beam gap		ASTM D256/ISO 179	40 kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256/ISO 179	27 kg·cm/cm(J/M)ft·lb/in
bending strength		ASTM D790/ISO 178	610 kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	20500 kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	108
tensile strength		ASTM D638/ISO 527	420 kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	R-108 R scale
Impact strength of cantilever beam gap	1/8"切口	ASTM D256	44 Kg/cm.cm
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	1/4"切口	ASTM D256	31 Kg/cm.cm
Bending modulus		ASTM D790	20500 kg/cm2

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	HDT	ASTM D648	86.0 °C
Vicat softening temperature		ASTM D1525	106.0 °C
Vicat softening temperature	Vicat softening temperature		ASTM D1525/ISO R306	105.5 ℃（℉）
Hot deformation temperature	HDT	ASTM D648/ISO 75	86 ℃（℉）
Hot deformation temperature	Hot deformation temperature	HDT	ASTM D648/ISO 75	97 ℃（℉）
Combustibility (rate)		UL 94	1/16

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	200℃*10kg	ISO 1133	10.0 g/10min
	melt mass-flow rate	200℃*5kg	ASTM D1238	0.8 g/10min
	melt mass-flow rate	melt mass-flow rate		ASTM D1238/ISO 1133	1 g/10min
density		ASTM D792/ISO 1183	1.05

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

ABS POLYLAC® PA-797 TAIWAN CHIMEI

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet