PA66 Zytel® 70G33HS1L NC010 DUPONT SHENZHEN

481

Unit Price:US$ 3,074 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
134MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜high strength｜Glass fiber reinforced
Application Areas:Automotive sector
Color:--
Grade:Enhanced level

Technical Data Sheet

Filling analysis	Test Method	Test Result
Odor	VDA 270	3.00
Emission of Organic Compounds	VDA 277	10.0 µgC/g
Top out temperature		210 °C

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	75 kJ/m²

flammability	Test Condition	Test Method	Test Result
雾化 - G-value (condensate)		ISO 6452	6.0E-4 g
FMVSS combustion rate		FMVSS 302	B
UL flame retardant rating		UL 94	HB
UL flame retardant rating	UL flame retardant rating		UL 94	HB
Burning rate	1.00 mm	ISO 3795	28 mm/min

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	11000 Mpa
tensile strength	Break	ISO 527-2	200 Mpa
Tensile strain	Break	ISO 527-2	3.0 %
Bending modulus		ISO 178	9500 Mpa
bending strength		ISO 178	280 Mpa

injection	Test Condition	Test Method	Test Result
Mold temperature			70 to 120 °C
Mold Temperature, Optimum			100 °C
Maintain pressure			50.0 to 100 Mpa
Maintain pressure	Maintain pressure	Drying Recommended		yes
Hold Pressure Time			3.00 s/mm
Drying time - hot air dryer			2.0 to 4.0 hr
drying temperature			80 °C
Melt Temperature, Optimum			285 °C
Processing (melt) temperature			275 to 295 °C
Suggested maximum moisture content			0.20 %
Maximum Screw Tangential Speed			12 m/min

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	Across Flow : 55 to 160°C	ISO 11359-2	1.4E-4 cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : -40 to 23°C	ISO 11359-2	6.5E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	8.3E-5 cm/cm/°C
			Linear coefficient of thermal expansion	Flow : 55 to 160°C	ISO 11359-2	1.3E-5 cm/cm/°C
				Linear coefficient of thermal expansion	Flow : -40 to 23°C	ISO 11359-2	2.4E-5 cm/cm/°C
				Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow	ISO 11359-2	1.8E-5 cm/cm/°C
Melting temperature		ISO 11357-3	262 °C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	252 °C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	261 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	横向Flow	ISO 294-4	1.1 %
Shrinkage rate	Shrinkage rate	Flow	ISO 294-4	0.30 %
Water absorption rate	Saturation, 23°C, 2.00 mm	ISO 62	5.7 %
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	1.8 %

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index		IEC 60112	V
Compared to the anti leakage trace index	Compared to the anti leakage trace index		UL 746	PLC 1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA66 Zytel® 70G33HS1L NC010 DUPONT SHENZHEN

Material Description

Technical Data Sheet Compare

Technical Data Sheet