PA66 Zytel® FR50 BK507 DUPONT JAPAN
232
- Unit Price:US$ 4,910 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:20MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜Glass fiber reinforced
- Application Areas:Fitness equipment｜Automotive sector｜Electrical field｜Electronic field｜Electrical appliances
- Color:--
- Grade:Wear resistant grade
Technical Data Sheet
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature | 1.8 MPa, Unannealed | ISO 75-2/A | 240 °C |
| Melting temperature | ISO 11357-3 | 262 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 | |
| UL 94 | V-0 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | 横向Flow | ISO 294-4 | 0.80 % |
| Flow | ISO 294-4 | 0.30 % | |
| Water absorption rate | 24 hr, 23°C, 2.00 mm | ISO 62 | 0.60 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface resistivity | IEC 62631-3-2 | -- ohms | |
| Volume resistivity | IEC 62631-3-1 | > 1.0E+13 ohms·m | |
| Dielectric strength | 2.00 mm | IEC 60243-1 | 24 KV/mm |
| Compared to the anti leakage trace index | IEC 60112 | PLC 2 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 80 °C | ||
| Drying time - hot air dryer | 2.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.20 % | ||
| Processing (melt) temperature | 280 to 300 °C | ||
| Melt Temperature, Optimum | 290 °C | ||
| Mold temperature | 70 to 120 °C | ||
| Mold Temperature, Optimum | 100 °C | ||
| Maintain pressure | 50.0 to 100 Mpa | ||
| Drying Recommended | yes | ||
| Hold Pressure Time | 3.00 s/mm | ||
| Maximum Screw Tangential Speed | 12 m/min |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 10200 Mpa | |
| tensile strength | Break | ISO 527-2 | 170 Mpa |
| Tensile strain | Break | ISO 527-2 | 2.6 % |
| impact performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -40°C | ISO 179/1eU | 50 kJ/m² |
| -30°C | ISO 179/1eU | 50 kJ/m² | |
| 23°C | ISO 179/1eU | 60 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.