'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PA66 Zytel® 70G43L BK DUPONT USA
356
- Unit Price:US$ 3,820 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:55MT
- Delivery Terms:FOB
- Port of Loading :Guangzhou port, China
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced｜high strength
- Application Areas:Electrical field｜Electronic field｜Fitness equipment
- Color:--
- Grade:Enhanced level
Material Certification
Technical Data Sheet
| Filling analysis | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Melt density | 1.29 | g/cm³ | ||
| Top out temperature | 210 | °C | ||
| Specific Heat Capacity of Melt | 2050 | J/kg/°C | ||
| Thermal Conductivity of Melt | 0.25 | W/m/K | ||
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 85 | kJ/m² |
| 23°C | ISO 179/1eU | 100 | kJ/m² | |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 110 | kJ/m² |
| 23°C | ISO 180/1U | 110 | kJ/m² | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| FMVSS combustion rate | FMVSS 302 | B | ||
| Extreme Oxygen Index | ISO 4589-2 | 23 | % | |
| UL flame retardant rating | UL 94 | HB | ||
| UL 94 | HB | |||
| Burning rate | 1.00 mm | ISO 3795 | 27 | mm/min |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Tensile modulus | ISO 527-2 | 14000 | Mpa | |
| tensile strength | Break | ISO 527-2 | 225 | Mpa |
| Tensile strain | Break | ISO 527-2 | 3.0 | % |
| Tensile creep modulus | 1 hr | ISO 899-1 | -- | Mpa |
| 1000 hr | ISO 899-1 | -- | Mpa | |
| Bending modulus | ISO 178 | 12000 | Mpa | |
| bending strength | ISO 178 | 340 | Mpa | |
| injection | Test Condition | Test Method | Test Result | Test Unit |
| drying temperature | 80 | °C | ||
| Drying time - hot air dryer | 2.0 to 4.0 | hr | ||
| Suggested maximum moisture content | 0.20 | % | ||
| Processing (melt) temperature | 285 to 305 | °C | ||
| Melt Temperature, Optimum | 295 | °C | ||
| Mold temperature | 70 to 120 | °C | ||
| Mold Temperature, Optimum | 100 | °C | ||
| Maintain pressure | 50.0 to 100 | Mpa | ||
| Drying Recommended | yes | |||
| Hold Pressure Time | 3.00 | s/mm | ||
| Maximum Screw Tangential Speed | 12 | m/min | ||
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Effective thermal diffusivity coefficient | 9.50E-8 | m²/s | ||
| Linear coefficient of thermal expansion | Across Flow : 55 to 160°C | ISO 11359-2 | 1.3E-4 | cm/cm/°C |
| Across Flow : -40 to 23°C | ISO 11359-2 | 6.1E-5 | cm/cm/°C | |
| Across Flow | ISO 11359-2 | 7.9E-5 | cm/cm/°C | |
| Flow : 55 to 160°C | ISO 11359-2 | 9.0E-6 | cm/cm/°C | |
| Flow : -40 to 23°C | ISO 11359-2 | 2.0E-5 | cm/cm/°C | |
| Flow | ISO 11359-2 | 1.5E-5 | cm/cm/°C | |
| Melting temperature | ISO 11357-3 | 262 | °C | |
| Vicat softening temperature | ISO 306/B50 | 255 | °C | |
| Glass transition temperature | ISO 11357-2 | 80.0 | °C | |
| Hot deformation temperature | 1.8 MPa, Unannealed | ISO 75-2/A | 255 | °C |
| 0.45 MPa, Unannealed | ISO 75-2/B | 262 | °C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Shrinkage rate | 横向Flow | ISO 294-4 | 1.0 | % |
| Flow | ISO 294-4 | 0.30 | % | |
| Water absorption rate | 24 hr, 23°C, 2.00 mm | ISO 62 | 0.90 | % |
| Saturation, 23°C, 2.00 mm | ISO 62 | 4.7 | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | ISO 62 | 1.5 | % | |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Dissipation factor | 1 MHz | IEC 62631-2-1 | 0.015 | |
| 100 Hz | IEC 62631-2-1 | 0.010 | ||
| Relative permittivity | 100 Hz | IEC 62631-2-1 | 4.50 | |
| 1 MHz | IEC 62631-2-1 | 4.10 | ||
| Dielectric strength | IEC 60243-1 | 27 | KV/mm | |
| Volume resistivity | IEC 62631-3-1 | > 1.0E+13 | ohms·m | |
| Surface resistivity | IEC 62631-3-2 | -- | ohms | |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | M -Sale | ISO 2039-2 | 105 | |
| R -Sale | ISO 2039-2 | 125 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.