PPO XYRON™ 100Z ASAHI JAPAN

Unit Price:US$ 3,640 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Transaction Guarantee:

Supplier Information

Dongguan Junlong Plastic & Chemical Co., Ltd.

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Chemical resistance｜Low temperature resistance
Application Areas:Fitness equipment｜Sports Equipment
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179	16	kJ/m²
machinability	Test Condition	Test Method	Test Result	Test Unit
Mold temperature			40-70	°C
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	5VA
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D-792	1.08
Shrinkage rate		ASTM D-955	0.50-0.70	%
Water absorption rate		ASTM D-570	0.10	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength		ASTM D-638	39	Mpa
Elongation at Break		ASTM D-638	40	%
Bending modulus		ASTM D-790	2350	Mpa
bending strength		ASTM D-790	59	Mpa
UL flame retardant rating		UL 94	V-0
Elongation at Break		ASTM D638/ISO 527	40	%
tensile strength		ASTM D638/ISO 527	36	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	R110
Bending modulus		ASTM D790/ISO 178	2250	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	59	kg/cm²(MPa)[Lb/in²]
tensile strength	Yield,23°C	ISO 527-2	37.0	Mpa
Nominal tensile fracture strain	23°C	ISO 527-2	30	%
Bending modulus	23°C	ISO 178	2370	Mpa
bending strength	23°C	ISO 178	66.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Combustibility (rate)		UL 94	V-0
Hot deformation temperature	HDT	ASTM D648/ISO 75	85	℃（℉）
Linear coefficient of thermal expansion	MD：-30to65°C	ISO 11359-2	8E-05	cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	78.0	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	85.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792/ISO 1183	1.08
Water absorption rate		ASTM D570/ISO 62	0.1	%
Shrinkage rate	2.00mm	Internal Method	0.50-0.70	%
Water absorption rate	23°C,24hr	ISO 62	0.10	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	1E+16	ohms
Volume resistivity	23°C	IEC 60093	1E+16	ohms·cm
Dielectric strength	2.00mm	IEC 60243-1	29	KV/mm
Dielectric constant	100Hz	IEC 60250	2.90
Dielectric constant	Dielectric constant	1MHz	IEC 60250	2.90
Dissipation factor	100Hz	IEC 60250	3E-03
Dissipation factor	Dissipation factor	1MHz	IEC 60250	4E-03

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
ASIAPLAS	US$ 3240 /MT

Supplier Join

Get App

Top

PPO XYRON™ 100Z ASAHI JAPAN

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index