PC/ABS CYCOLOY™ C2950-701 SABIC INNOVATIVE SAUDI
245
- Unit Price:US$ 2,831 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:30MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Halogen-free flame retardant｜High temperature resistance｜Medium viscosity
- Application Areas:Automotive components｜Electronic and electrical components
- Color:--
- Grade:Injection grade
Technical Data Sheet
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hardness (Rockwell R) | ASTM D785 | 123 R |
| Electrical Property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 100000000000000000 ohm-cm | |
| Surface resistivity | ASTM D257 | 10000000000000000 Ohm | |
| Dielectric constant | ASTM D 150 | 3 | |
| ASTM D 150 | 3 | ||
| Dissipation factor | ASTM D 150 | 50 E-4 | |
| ASTM D 150 | 49 E-4 | ||
| Compared to the Leakage Traceability Index (CTI) | UL 746A | PLC_0 | |
| Dielectric strength | in oil, 3.2 | ASTM D149 | 19.5 kV/mm |
| Arc resistance | ASTM D495 | PLC_6 | |
| High voltage arc tracing rate | UL 746A | PLC 2 | |
| Hot wire ignition (HWI) | UL 746A | PLC_1 | |
| High current arc ignition (HAI) | UL 746A | PLC_0 |
| thermal properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Vicat softening temperature | Rate B/50 | ASTM D1525 | 85 °C |
| RTI Imp | UL 746B | 85 °C | |
| RTI Elec | UL 746B | 85 °C | |
| RTI Imp | UL 746B | 85 °C | |
| Linear coefficient of thermal expansion | -30°C to 3，Flow | ASTM E831 | 72 E-6/°C |
| -30°C to 3，Across Flow | ASTM E831 | 72 E-6/°C | |
| thermal conductivity | ASTM C 177 | 0.2 W/m-°C |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 10 g/10min | |
| Shrinkage rate | flow, 3.2 | Internal | 0.4-0.8 |
| xflow, 3.2 | Internal | 0.4-0.6 | |
| Water absorption rate | flow, 3.2 | ASTM D570 | 0.4 |
| 24 hours | ASTM D570 | 0.1 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | Type I, 50，Yield | ASTM D638 | 62 Mpa |
| Elongation at Break | Type I, 50 | ASTM D638 | 40 |
| bending strength | 2.6 mm/，Yield | ASTM D790 | 102 Mpa |
| Bending modulus | 2.6 mm/ | ASTM D790 | 2650 Mpa |
| impact performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | 30℃ | ASTM D256 | 160 J/m |
| 23℃ | ASTM D256 | 534 J/m | |
| Instrumented dart impact energy -30 ℃ (-22 ℉) peak | ASTM D3763 | 54 J | |
| Instrumented dart impact energy 23 ℃ (73 ℉) total energy | ASTM D3763 | 61 J |
| combustion performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL fire rating V | UL 94 | 1.5 mm | |
| UL fire rating 5VB | UL 94 | 2.49 mm | |
| Limiting Oxygen Index (LOI) | ASTM D 2863 | 32 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.