Material Description
- Material Properties:Resistance to stress cracking｜High toughness｜Heat sealing performance
- Application Areas:Food service sector｜Soft packaging composite materials Liquid packaging composite materials
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ISO 306 | 81.1 ℃ | |
| melting temperature | Internal Method | 97.8 ℃ | |
| vicat | ASTM D-1525 | 81.1 ℃ | |
| ASTMD1525 | 81.1 °C | ||
| melting temperature | 内部方法 | 97.8 °C |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Monomer content | Internal Method | 9.7 % | |
| melt mass-flow rate | 190℃/2.16kg | ASTM D-1238 | 11 g/10min |
| 190℃/2.16kg | ISO 1133 | 11 g/10min |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Starting temperature of heat sealing | Internal Method | 85 ℃ | |
| Water Vapor Transmission Rate | 38℃，90% RH | DIN 53122/2 | 0.41 g·mm/m2/atm/24hr |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Initial sealing temperature | 内部方法 | 85.0 °C | |
| Water Vapor Transmission Rate | 38°C,90%RH | DIN 53122/2 | 0.41 g·mm/m²/atm/24hr |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D-792 | 0.938 g/cm³ | |
| ISO 1183 | 0.938 g/cm³ | ||
| ASTMD792 | 0.938 g/cm³ | ||
| melt mass-flow rate | 190°C/2.16kg | ASTMD1238 | 11 g/10min |
| Content of comonomer | 内部方法 | 9.7 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 屈服,Compression Molded | ASTM D-638 | 7.93 MPa |
| 屈服,Compression Molded | ISO 527-2 | 7.93 MPa | |
| Compression Molded，断裂 | ASTM D-638 | 17.6 MPa | |
| Compression Molded，断裂 | ISO 527-2 | 17.6 MPa | |
| Elongation at break | Compression Molded | ASTM D-638 | 600 % |
| Compression Molded | ISO 527-2 | 600 % | |
| tensile strength | 屈服,模压成型 | ASTMD638 | 7.93 Mpa |
| 断裂,模压成型 | ASTMD638 | 17.6 Mpa | |
| elongation | 断裂,模压成型 | ASTMD638 | 600 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.