PBT/PET T7331 COVESTRO GERMANY
314
- Unit Price:US$ 2,343 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:33MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Easy to form|High impact
- Application Areas:Automotive Applications|Automotive interior parts
- Color:--
- Grade:Injection grade
Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|---|---|---|
Apparent density | ISO 60 | 0.80 g/cm³ | |
Melt volume flow rate | ISO 1133 | 30.0 cm3/10min | |
Shrinkage rate | ISO 294-4 | 0.90 % | |
ISO 294-4 | 0.20 % | ||
ISO 294-4 | 0.30 % | ||
ISO 294-4 | 0.10 % | ||
Water absorption rate | ISO 62 | 0.30 % | |
ISO 62 | 0.10 % | ||
Viscosity value | ISO 1628 | 91.0 ml/g |
hardness | Test Condition | Test Method | Test Result |
---|---|---|---|
ball-indentation hardness | ISO 2039-1 | 200 Mpa |
flammability | Test Condition | Test Method | Test Result |
---|---|---|---|
UL flame retardant rating | UL 94 | HB | |
UL 94 | HB | ||
Burning wire flammability index | IEC 60695-2-12 | 750 °C | |
Limiting Oxygen Index | ISO 4589-2 | 21 % |
Supplementary Information | Test Condition | Test Method | Test Result |
---|---|---|---|
electrolytic corrosion | IEC 60426 | A1 | |
ISO Shortcut | ISO 7792 | PBT+PET.GHLMR.09-100.GF30 |
Mechanical properties | Test Condition | Test Method | Test Result |
---|---|---|---|
Flexural modulus | ISO 178/A | 10300 Mpa | |
bending strength | ASTM D790 | 207 Mpa | |
ISO 178 | 230 Mpa | ||
Bending Strain | 3.0 % | ||
Tensile modulus | ASTM D638 | 9980 Mpa | |
ISO 527-2/1 | 10400 Mpa | ||
tensile strength | ASTM D638 | 123 Mpa | |
ISO 527-2/5 | 145 Mpa | ||
elongation | ASTM D638 | 2.5 % | |
Tensile strain | ISO 527-2/5 | 2.8 % | |
Tensile creep modulus | ISO 899-1 | 10000 Mpa | |
ISO 899-1 | 8500 Mpa | ||
Flexural modulus | ASTM D790 | 8550 Mpa |
Impact resistance | Test Condition | Test Method | Test Result |
---|---|---|---|
Impact strength of simply supported beam without notch | ISO 179/1eU | 55 kJ/m² | |
ISO 179/1eU | 65 kJ/m² | ||
Suspended wall beam without notch impact strength | ISO 180/1U | 55 kJ/m² | |
ISO 180/1U | 55 kJ/m² |
film | Test Condition | Test Method | Test Result |
---|---|---|---|
Thin film puncture strength | ISO 6603-2 | 2.10 J | |
ISO 6603-2 | 650 N |
Electrical performance | Test Condition | Test Method | Test Result |
---|---|---|---|
dielectric strength | IEC 60243-1 | 27 KV/mm | |
relative permittivity | IEC 60250 | 4.00 | |
IEC 60250 | 3.80 | ||
Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 |
Thermal performance | Test Condition | Test Method | Test Result |
---|---|---|---|
TemperatureIndex | IEC 60216 | 155 | |
IEC 60216 | 140 | ||
IEC 60216 | 155 | ||
melting temperature | ISO 11357-3 | 225to250 °C | |
Linear coefficient of thermal expansion | ISO 11359-2 | 3E-05 cm/cm/°C | |
ISO 11359-2 | 6E-05 cm/cm/°C | ||
thermal conductivity | ISO 8302 | 0.27 W/m/K | |
RTI Elec | UL 746 | 140 °C | |
RTI Imp | UL 746 | 125 °C | |
RTI Str | UL 746 | 140 °C | |
Half Interval | IEC 60216 | 13.5 °C | |
IEC 60216 | 10.2 °C | ||
IEC 60216 | 10.2 °C | ||
Heat distortion temperature | ISO 75-2/B | 220 °C | |
ISO 75-2/A | 200 °C | ||
vicat | ISO 306/B120 | 205 °C | |
ball-indentation hardness | IEC 60695-10-2 | Pass |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.