PPA

PPA LNP™ LUBRICOMP™ UFL-4036 BK8115 SABIC INNOVATIVE US

250

Unit Price:US$ 4,940 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
36MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜Flame retardant
Application Areas:tubing｜Lighting applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Multi axis Instrumented Impact Energy		ISO 6603-2	2.00 J
Impact strength of cantilever beam gap	23°C	ISO 180/1A	9.1 kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	47 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	8.90 J

mechanical properties	Test Condition	Test Method	Test Result
Friction coefficient	Dynamic	ASTM D3702Modified	0.48
Friction coefficient	Friction coefficient	Static	ASTM D3702Modified	0.52
bending strength	Break,50.0mmSpan	ASTM D790	233 Mpa
bending strength	bending strength	Yield,50.0mmSpan	ASTM D790	242 Mpa
Bending modulus		ISO 178	11300 Mpa
Bending modulus	Bending modulus	50.0mmSpan	ASTM D790	10600 Mpa
Tensile strain	Break	ISO 527-2/5	2.0 %
elongation	Break	ASTM D638	1.7 %
Tensile strain	Yield	ISO 527-2/5	2.0 %
elongation	Yield	ASTM D638	1.8 %
tensile strength	Break	ISO 527-2/5	192 Mpa
	tensile strength	Break	ASTM D638	189 Mpa
		tensile strength	Yield	ISO 527-2/5	192 Mpa
		tensile strength	tensile strength	Yield	ASTM D638	189 Mpa
Tensile modulus		ISO 527-2/1	12600 Mpa
	Tensile modulus	--3	ASTM D638	15400 Mpa
	Tensile modulus	Tensile modulus	--2	ASTM D638	15400 Mpa
Wear factor	Ring	ASTM D3702Modified	0.100 10^-10in^5-min/ft-lb-hr
Wear factor	Wear factor	Washer	ASTM D3702Modified	5.00 10^-10in^5-min/ft-lb-hr

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD：-30to30°C	ASTM D696	4.5E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-30to30°C	ASTM D696	2.1E-05 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	273 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	277 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD：24hr	ASTM D955	0.20-0.40 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.25 %
Water absorption rate	Water absorption rate	24hr,50%RH	ASTM D570	0.15 %
Shrinkage rate	TD：24hr	ASTM D955	0.80-1.0 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PPA LNP™ LUBRICOMP™ UFL-4036 BK8115 SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet