TPV

TPV Santoprene™ 111-35 CELANESE USA

413

Unit Price:US$ 5,270 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
44MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Aging resistance
Application Areas:Electrical field｜Electronic field｜Bottle cap｜Automotive sector｜Printing machine parts｜Phone｜Architectural application field｜Washer｜packing｜sporting goods｜Application in the automotive field
Color:--
Grade:Weather resistant grade

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	HB

elastomer	Test Condition	Test Method	Test Result
Permanent compression deformation	125°C,70hr	ISO 815	31 %
	Permanent compression deformation	23°C,22hr	ISO 815	10 %
		Permanent compression deformation	125°C,70hr	ASTM D395B	31 %
		Permanent compression deformation	Permanent compression deformation	23°C,22hr	ASTM D395B	10 %
tear strength	23°C，Across Flow (Across Flow)	ISO 34-1	10 kN/m
tear strength	tear strength	23°C，横向Flow	ASTM D624	10.0 kN/m
elongation	Break,23°C，Across Flow	ISO 37	330 %
elongation	elongation	Break,23°C，Across Flow	ASTM D412	330 %
tensile strength	Break,23°C	ISO 37	2.90 Mpa
tensile strength	tensile strength	Break,23°C，横向Flow	ASTM D412	2.90 Mpa
Tensile stress	100%Strain,23°C，横向Flow	ISO 37	1.00 Mpa
Tensile stress	Tensile stress	100%Strain,23°C，横向Flow	ASTM D412	1.00 Mpa

thermal performance	Test Condition	Test Method	Test Result
Brittle temperature		ISO 812	-63.0 °C
Brittle temperature	Brittle temperature		ASTM D746	-63.0 °C

hardness	Test Condition	Test Method	Test Result
Shore hardness	ShoreA,15Sec,23°C	ISO 868	38

aging	Test Condition	Test Method	Test Result
Change rate of hardness (Shore) in the air	ShoreA,125°C,168hr,inIRM903Oil	ASTM D471	-30
	Change rate of hardness (Shore) in the air	ShoreA,100°C,168hr,inIRM903Oil	ASTM D471	-26
		Change rate of hardness (Shore) in the air	ShoreA,100°C,168hr,inDeionizedWater	ASTM D471	0.0
			Change rate of hardness (Shore) in the air	ShoreA,23°C,168hr,inTrichloroethylene	ASTM D471	1.0
				Change rate of hardness (Shore) in the air	ShoreA,23°C,168hr,inSulfuricAcid,98%	ASTM D471	-2.0
					Change rate of hardness (Shore) in the air	ShoreA,23°C,168hr,inSodiumHydroxide,50%	ASTM D471	4.0
						Change rate of hardness (Shore) in the air	ShoreA,23°C,168hr,inSodiumChloride,15%	ASTM D471	2.0
							Change rate of hardness (Shore) in the air	ShoreA,23°C,168hr,inMethylethylketone	ASTM D471	15
								Change rate of hardness (Shore) in the air	ShoreA,23°C,168hr,inIsopropylAlcohol	ASTM D471	5.0
								Change rate of hardness (Shore) in the air	Change rate of hardness (Shore) in the air	ShoreA,23°C,168hr,inHydrochloricAcid,10%	ASTM D471	-1.0
Change rate of tensile strength in air	150°C,168hr	ASTM D573	-29 %
Change rate of tensile strength in air	Change rate of tensile strength in air	150°C,168hr	ISO 188	-29 %
Change rate of ultimate elongation in air	150°C,168hr	ASTM D573	-1.0 %
Hardness change rate in the air	ShoreA,150°C,168hr	ASTM D573	-1.0
Shore hardness	ShoreA,150°C,168hr	ISO 188	-1.0
Change rate of tensile strength in air	23°C,168hr,inAceticAcid	ASTM D471	-6.0 %
	Change rate of tensile strength in air	23°C,168hr,inCyclohexane	ASTM D471	4040 %
		Change rate of tensile strength in air	23°C,168hr,inDetergent(Tide),2.5%	ASTM D471	-6.0 %
		Change rate of tensile strength in air	Change rate of tensile strength in air	23°C,168hr,inEthanol,95%	ASTM D471	-8.0 %
Change rate of ultimate elongation in air	23°C,168hr,inHydrochloricAcid,10%	ASTM D471	0.0 %
	Change rate of ultimate elongation in air	23°C,168hr,inIsopropylAlcohol	ASTM D471	53 %
		Change rate of ultimate elongation in air	23°C,168hr,inMethylethylketone	ASTM D471	80 %
			Change rate of ultimate elongation in air	23°C,168hr,inSodiumChloride,15%	ASTM D471	-7.0 %
				Change rate of ultimate elongation in air	23°C,168hr,inSodiumHydroxide,50%	ASTM D471	-3.0 %
					Change rate of ultimate elongation in air	23°C,168hr,inSulfuricAcid,98%	ASTM D471	-10 %
						Change rate of ultimate elongation in air	23°C,168hr,inTrichloroethylene	ASTM D471	77 %
							Change rate of ultimate elongation in air	100°C,168hr,inDeionizedWater	ASTM D471	-17 %
								Change rate of ultimate elongation in air	100°C,168hr,inIRM903Oil	ASTM D471	-63 %
								Change rate of ultimate elongation in air	Change rate of ultimate elongation in air	125°C,70hr,inIRM903Oil	ASTM D471	-65 %
Change rate of tensile strength in air	125°C,168hr,inIRM903Oil	ASTM D471	-67 %
	Change rate of tensile strength in air	23°C,168hr,inIsopropylAlcohol	ISO 1817	27 %
		Change rate of tensile strength in air	23°C,168hr,inMethylethylketone	ISO 1817	43 %
			Change rate of tensile strength in air	23°C,168hr,inSodiumChloride,15%	ISO 1817	-14 %
				Change rate of tensile strength in air	23°C,168hr,inAceticAcid	ISO 1817	-6.0 %
					Change rate of tensile strength in air	23°C,168hr,inCyclohexane	ISO 1817	4040 %
						Change rate of tensile strength in air	23°C,168hr,inDetergent(Tide),2.5%	ISO 1817	-6.0 %
							Change rate of tensile strength in air	23°C,168hr,inEthanol,95%	ISO 1817	-8.0 %
							Change rate of tensile strength in air	Change rate of tensile strength in air	23°C,168hr,inHydrochloricAcid,10%	ISO 1817	-6.0 %
Shore hardness	ShoreA,23°C,168hr,inMethylethylketone	ISO 1817	15
Shore hardness	Shore hardness	ShoreA,23°C,168hr,inSodiumChloride,15%	ISO 1817	2.0
Change rate of tensile strength in air	23°C,168hr,inSodiumHydroxide,50%	ISO 1817	-5.0 %
Quality change rate	23.0°C,168hr,inTrichloroethylene	ISO 1817	-20 %
	Quality change rate	23.0°C,168hr,inCyclohexane	ISO 1817	-11 %
		Quality change rate	23.0°C,168hr,inSodiumHydroxide,50%	ISO 1817	-0.30 %
			Quality change rate	23.0°C,168hr,inSodiumChloride,15%	ISO 1817	0.10 %
				Quality change rate	23.0°C,168hr,inHydrochloricAcid,10%	ISO 1817	0.20 %
					Quality change rate	23.0°C,168hr,inEthanol,95%	ISO 1817	0.20 %
						Quality change rate	23.0°C,168hr,inDetergent(Tide),2.5%	ISO 1817	0.90 %
							Quality change rate	100°C,168hr,inDeionizedWater	ISO 1817	6.2 %
								Quality change rate	23.0°C,168hr,inAceticAcid	ISO 1817	6.9 %
								Quality change rate	Quality change rate	23.0°C,168hr,inSulfuricAcid,98%	ISO 1817	7.2 %
Shore hardness	ShoreA,23°C,168hr,inAceticAcid	ISO 1817	-1.0
	Shore hardness	ShoreA,23°C,168hr,inCyclohexane	ISO 1817	-11
		Shore hardness	ShoreA,23°C,168hr,inDetergent(Tide),2.5%	ISO 1817	2.0
			Shore hardness	ShoreA,23°C,168hr,inEthanol,95%	ISO 1817	1.0
				Shore hardness	ShoreA,23°C,168hr,inHydrochloricAcid,10%	ISO 1817	-1.0
					Shore hardness	ShoreA,23°C,168hr,inIsopropylAlcohol	ISO 1817	5.0
						Shore hardness	ShoreA,23°C,168hr,inSodiumHydroxide,50%	ISO 1817	4.0
						Shore hardness	Shore hardness	ShoreA,23°C,168hr,inSulfuricAcid,98%	ISO 1817	-2.0
Quality change rate	23°C,168hr,inMethylethylketone	ASTM D471	-41 %
	Quality change rate	23°C,168hr,inSodiumChloride,15%	ASTM D471	0.10 %
		Quality change rate	23°C,168hr,inSodiumHydroxide,50%	ASTM D471	-0.30 %
			Quality change rate	23°C,168hr,inSulfuricAcid,98%	ASTM D471	7.2 %
				Quality change rate	23°C,168hr,inTrichloroethylene	ASTM D471	-20 %
					Quality change rate	100°C,168hr,inDeionizedWater	ASTM D471	6.2 %
						Quality change rate	100°C,168hr,inIRM903Oil	ASTM D471	93 %
							Quality change rate	125°C,168hr,inIRM903Oil	ASTM D471	100 %
								Quality change rate	23.0°C,168hr,inMethylethylketone	ISO 1817	-41 %
								Quality change rate	Quality change rate	23.0°C,168hr,inIsopropylAlcohol	ISO 1817	-25 %
Change rate of tensile strength in air	23°C,168hr,inSulfuricAcid,98%	ISO 1817	-47 %
	Change rate of tensile strength in air	23°C,168hr,inTrichloroethylene	ISO 1817	56 %
		Change rate of tensile strength in air	100°C,168hr,inDeionizedWater	ISO 1817	-18 %
			Change rate of tensile strength in air	100°C,168hr,inIRM903Oil	ISO 1817	-57 %
				Change rate of tensile strength in air	125°C,70hr,inIRM903Oil	ISO 1817	-61 %
				Change rate of tensile strength in air	Change rate of tensile strength in air	125°C,168hr,inIRM903Oil	ISO 1817	-67 %
Change rate of ultimate elongation in air	23°C,168hr,inAceticAcid	ASTM D471	-3.0 %
	Change rate of ultimate elongation in air	23°C,168hr,inCyclohexane	ASTM D471	63 %
		Change rate of ultimate elongation in air	23°C,168hr,inDetergent(Tide),2.5%	ASTM D471	0.0 %
		Change rate of ultimate elongation in air	Change rate of ultimate elongation in air	23°C,168hr,inEthanol,95%	ASTM D471	3.0 %
Change rate of tensile strength in air	23°C,168hr,inHydrochloricAcid,10%	ASTM D471	-6.0 %
	Change rate of tensile strength in air	23°C,168hr,inSodiumChloride,15%	ASTM D471	-14 %
		Change rate of tensile strength in air	23°C,168hr,inIsopropylAlcohol	ASTM D471	27 %
			Change rate of tensile strength in air	23°C,168hr,inMethylethylketone	ASTM D471	43 %
				Change rate of tensile strength in air	23°C,168hr,inSodiumHydroxide,50%	ASTM D471	-5.0 %
					Change rate of tensile strength in air	23°C,168hr,inSulfuricAcid,98%	ASTM D471	-47 %
						Change rate of tensile strength in air	23°C,168hr,inTrichloroethylene	ASTM D471	56 %
							Change rate of tensile strength in air	100°C,168hr,inDeionizedWater	ASTM D471	-18 %
								Change rate of tensile strength in air	100°C,168hr,inIRM903Oil	ASTM D471	-57 %
								Change rate of tensile strength in air	Change rate of tensile strength in air	125°C,70hr,inIRM903Oil	ASTM D471	-61 %
Change rate of ultimate elongation in air	125°C,168hr,inIRM903Oil	ASTM D471	-70 %
Tensile stress change rate	23°C,168hr,inAceticAcid，Break	ISO 1817	-3.0 %
	Tensile stress change rate	23°C,168hr,inCyclohexane，Break	ISO 1817	63 %
		Tensile stress change rate	23°C,168hr,inDetergent(Tide),2.5%，Break	ISO 1817	0.0 %
			Tensile stress change rate	23°C,168hr,inEthanol,95%，Break	ISO 1817	3.0 %
				Tensile stress change rate	23°C,168hr,inHydrochloricAcid,10%，Break	ISO 1817	0.0 %
					Tensile stress change rate	23°C,168hr,inIsopropylAlcohol，Break	ISO 1817	53 %
						Tensile stress change rate	23°C,168hr,inMethylethylketone，Break	ISO 1817	80 %
							Tensile stress change rate	23°C,168hr,inSodiumChloride,15%，Break	ISO 1817	-7.0 %
								Tensile stress change rate	23°C,168hr,inSodiumHydroxide,50%，Break	ISO 1817	-3.0 %
								Tensile stress change rate	Tensile stress change rate	23°C,168hr,inSulfuricAcid,98%，Break	ISO 1817	-10 %
Quality change rate	23°C,168hr,inDetergent(Tide),2.5%	ASTM D471	0.90 %
Tensile stress change rate	23°C,168hr,inTrichloroethylene，Break	ISO 1817	77 %
Shore hardness	ShoreA,23°C,168hr,inTrichloroethylene	ISO 1817	1.0
Shore hardness	Shore hardness	ShoreA,100°C,168hr,inDeionizedWater	ISO 1817	0.0
Quality change rate	23°C,168hr,inEthanol,95%	ASTM D471	0.20 %
	Quality change rate	23°C,168hr,inHydrochloricAcid,10%	ASTM D471	0.20 %
		Quality change rate	23°C,168hr,inIsopropylAlcohol	ASTM D471	-25 %
			Quality change rate	100°C,168hr,inIRM903Oil	ISO 1817	93 %
			Quality change rate	Quality change rate	125°C,168hr,inIRM903Oil	ISO 1817	100 %
Volume change	125°C,70hr,在IRM903油中	ASTM D471	110 %
Volume change	Volume change	125°C,70hr,在IRM903油中	ISO 1817	110 %
Shore hardness	ShoreA,100°C,168hr,inIRM903Oil	ISO 1817	-26
Shore hardness	Shore hardness	ShoreA,125°C,168hr,inIRM903Oil	ISO 1817	-30
Quality change rate	23°C,168hr,inAceticAcid	ASTM D471	6.9 %
Quality change rate	Quality change rate	23°C,168hr,inCyclohexane	ASTM D471	-11 %
Change rate of hardness (Shore) in the air	ShoreA,23°C,168hr,inDetergent(Tide),2.5%	ASTM D471	2.0
Tensile stress change rate	23°C,168hr,inTrichloroethylene，Break	ISO 1817	77 %
	Tensile stress change rate	100°C,168hr,inDeionizedWater，Break	ISO 1817	-17 %
		Tensile stress change rate	100°C,168hr,inIRM903Oil，Break	ISO 1817	-63 %
			Tensile stress change rate	125°C,70hr,inIRM903Oil，Break	ISO 1817	-65 %
			Tensile stress change rate	Tensile stress change rate	125°C,168hr,inIRM903Oil，Break	ISO 1817	-70 %
Change rate of hardness (Shore) in the air	ShoreA,23°C,168hr,inAceticAcid	ASTM D471	-1.0
	Change rate of hardness (Shore) in the air	ShoreA,23°C,168hr,inAceticAcid	ASTM D471	-1.0
		Change rate of hardness (Shore) in the air	ShoreA,23°C,168hr,inCyclohexane	ASTM D471	-11
		Change rate of hardness (Shore) in the air	Change rate of hardness (Shore) in the air	ShoreA,23°C,168hr,inEthanol,95%	ASTM D471	1.0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

TPV Santoprene™ 111-35 CELANESE USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet