PA6T

PA6T Zytel® HTNFR52G30NH BL563 DUPONT USA

265

Unit Price:US$ 6,404 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
25MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced｜Flame retardant
Application Areas:Electrical field｜Electronic field｜Electrical appliances｜Automotive sector
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	kJ/m²	45
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	kJ/m²	40

flammability	Test Condition	Test Method	Test Result
Extreme Oxygen Index		%	37 --
Burning wire flammability index	3.00mm	°C	960 --
Burning wire flammability index	Burning wire flammability index	0.400mm	°C	960 --
Flammability level	1.50mm		V-0 --
Flammability level	Flammability level	0.400mm		V-0 --
Hot filament ignition temperature	3.00mm	°C	775 --
Hot filament ignition temperature	Hot filament ignition temperature	0.400mm	°C	700 --

mechanical properties	Test Condition	Test Method	Test Result
bending strength			225 MPa
Bending modulus		MPa	9800 10800
Tensile strain	Break	%	2.1 1.9
tensile strength	Break		145 MPa
Tensile modulus		MPa	10700 11300

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	MD:-40to23°C	cm/cm/°C	1.8E-05 --
	Linear coefficient of thermal expansion	MD:55to160°C	cm/cm/°C	1.2E-05 --
		Linear coefficient of thermal expansion	TD	cm/cm/°C	6.2E-05 --
			Linear coefficient of thermal expansion	TD:-40to23°C	cm/cm/°C	6E-05 --
			Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	cm/cm/°C	1.8E-05 --
Melting temperature		°C	310 --
Hot deformation temperature	1.8MPa,Unannealed	°C	281 --
RTI Elec	3.00mm	°C	140 --
	RTI Elec	1.50mm	°C	140 --
		RTI Elec	0.750mm	°C	140 --
		RTI Elec	RTI Elec	0.400mm	°C	140 --
Linear coefficient of thermal expansion	TD:55to160°C	cm/cm/°C	9.5E-05 --

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD	%	0.30 --
Shrinkage rate	Shrinkage rate	TD	%	1.0 --

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index		V	PLC 0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA6T Zytel® HTNFR52G30NH BL563 DUPONT USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet