PBT

PBT VALOX™ 3706-1001 SABIC INNOVATIVE SHANGHAI

261

Unit Price:US$ 4,575 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Impact modification
Application Areas:Plastic bag｜Electrical appliances｜Construction field｜Outdoor applications｜Lighting applications｜Electronic field｜Electrical field
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C,TotalEnergy	ASTM D3763	49.7 J
Impact strength of cantilever beam gap	23°C	ASTM D256	670 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	2.5mm	UL 94	5VA
UL flame retardant rating	UL flame retardant rating	1.5mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Yield,50.0mmSpan	ASTM D790	78.6 Mpa
Bending modulus	50.0mmSpan	ASTM D790	2000 Mpa
elongation	Break	ASTM D638	50 %
elongation	elongation	Yield	ASTM D638	6.0 %
tensile strength	Break	ASTM D638	39.3 Mpa
tensile strength	tensile strength	Yield	ASTM D638	49.0 Mpa
Tensile modulus		ASTM D638	1970 Mpa

thermal performance	Test Condition	Test Method	Test Result
RTI Imp		UL 746	85.0 °C
RTI Str		UL 746	100 °C
RTI Elec		UL 746	100 °C
Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	8.6E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	7.9E-05 cm/cm/°C
Vicat softening temperature		ASTM D15255	135 °C
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	85.0 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	127 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	TD：3.20mm	Internal Method	1.2-1.4 %
Shrinkage rate	Shrinkage rate	MD：3.20mm	Internal Method	1.2-1.4 %
Melt Volume Flow Rate (MVR)	265°C/5.0kg	ISO 1133	17.0 cm3/10min
melt mass-flow rate	266°C/5.0kg	ASTM D1238	19 g/10min
density		ASTM D792	1.30 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Arc resistance		ASTM D495	PLC6
Hot wire ignition	HWI	UL 746	PLC 2
High voltage arc tracing rate	HVTR	UL 746	PLC 4
Compared to the anti leakage trace index	CTI	UL 746	PLC 2
High arc combustion index	HAI	UL 746	PLC 0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PBT VALOX™ 3706-1001 SABIC INNOVATIVE SHANGHAI

Material Description

Technical Data Sheet Compare

Technical Data Sheet