PA12 UBESTA 3014U UBE JAPAN
344
- Unit Price:US$ 13,978 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility｜Low viscosity
- Application Areas:Automotive sector｜Industrial applications
- Color:--
- Grade:Extrusion grade
Material Certification
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting temperature | 176-180 ℃（℉） | ||
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 10 mm/mm.℃ | |
| Heat Deflection Temperature | 0.45Mpa | ISO 75-2 | 95 °C |
| 1.8Mpa | ISO 75-2 | 45 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 1.3 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | ASTM D257/IEC 60093 | 10^15 Ω.cm | |
| IEC 60093 | 10 Ω.cm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.02 kg·cm/cm(J/M)ft·lb/in | |
| Water absorption rate | ASTM D570/ISO 62 | 0.25 % | |
| melting temperature | ISO 11357-3 | 179 °C | |
| shrinkage rate | ISO 294-4 | 0.9/0.9 % | |
| Water absorption rate | ISO 62 | 0.6 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 5 kg·cm/cm(J/M)ft·lb/in | |
| Rockwell hardness | ASTM D785 | 110 | |
| flexural modulus | ASTM D412/ISO 527 | 14500 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 560 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | 屈服 | ISO 527-1/-2 | 47 Mpa |
| Tensile modulus | 屈服 | ISO 527-1/-2 | 4 % |
| elongation | 断裂 | ISO 527-1/-2 | ＞200 % |
| bending strength | ISO 178 | 60 Mpa | |
| flexural modulus | ISO 178 | 1500 Mpa | |
| Shore hardness | ISO 868 | 77 D | |
| Rockwell hardness | ISO 2039-2 | 105 R | |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 3C KJ/m |
| -40℃ | ISO 179/1eA | 3C KJ/m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.