PC PANLITE® ML-5206ZHP TEIJIN JAPAN
173
- Unit Price:US$ 5,028 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Thermal stability｜transparent
- Application Areas:Casters｜Fitness equipment
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO 75-2/A | 123 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 7E-05 cm/cm/°C |
| TD | ISO 11359-2 | 7E-05 cm/cm/°C | |
| RTI Elec | 1.5mm | UL 746 | 130 °C |
| RTI Imp | 1.5mm | UL 746 | 125 °C |
| RTI | 1.5mm | UL 746 | 130 °C |
| Heat Deflection Temperature | 1.80MPa | ISO 75-1 | 123 °C |
| 阻燃性，1.5mm(3.2mm) | UL 94 | V-0(5VA) |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| transmissivity | 3000µm | ASTM D1003 | 77.0 % |
| transmittance | 1.5mmt | JIS K7136 | 85 % |
| Pigment dispersion | 2.0mmt | In-house method | 17 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| 3.2mm | UL 94 | 5VA | |
| Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 960 °C |
| 3.0mm | IEC 60695-2-12 | 960 °C | |
| Hot filament ignition temperature | 1.5mm | IEC 60695-2-13 | 850 °C |
| 3.0mm | IEC 60695-2-13 | 850 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 无断裂 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 2.50 cm3/10min |
| shrinkage rate | TD:4.00mm | 内部方法 | 0.50-0.70 % |
| MD:4.00mm | 内部方法 | 0.50-0.70 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.20 % |
| Dissolving fingers | 300℃ | ISO 1133 | 2.5 cm310min |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2400 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 65.0 Mpa |
| 断裂 | ISO 527-2/50 | 53.0 Mpa | |
| Tensile strain | 屈服 | ISO 527-2/50 | 6.0 % |
| Nominal tensile fracture strain | ISO 527-2/50 | 25 % | |
| flexural modulus | ISO 178 | 2350 Mpa | |
| bending strength | ISO 178 | 97.0 Mpa | |
| Elongation at break | 50mm/min | ISO 527-1 | 25 % |
| flexural modulus | 2mm/min | ISO 178 | 2350 Mpa |
| bending strength | 2mm/min | ISO 178 | 97 Mpa |
| Impact strength of cantilever beam gap | Notched | ISO 179 | 9.0 kJ/m² |
| tensile strength | 50mm/min，屈服 | ISO 527-1 | 65 Mpa |
| 50mm/min，断裂 | ISO 527-1 | 53 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.