Material Properties:Flame retardant｜Glass fiber reinforced
Application Areas:Office supplies｜Automotive sector｜building materials｜Electronic field｜Electrical field
Color:--
Grade:--

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result
filler content			20 wt%
Water absorption rate		D570	0.4 %
Water absorption rate	Water absorption rate		D570	4.5 %
Rockwell hardness		D785	150 R

processability	Test Condition	Test Method	Test Result
Shrinkage rate			0.4-0.6 %
Shrinkage rate	Shrinkage rate			0.8-1.2 %

Mechanical properties	Test Condition	Test Method	Test Result
tensile strength		D638	130 Mpa
elongation at break		D638	5 %
bending strength		D790	210 Mpa
Flexural modulus		D790	7.0 GPa
Impact strength of cantilever beam gap		D256	80 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		D256	50 kJ/m²
wear resistance		D1044	25 mg/1000

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		D257	1013 Ω.m
dielectric strength		D149	31 MV/m

Thermal performance	Test Condition	Test Method	Test Result
melting temperature		DSC	265 °C
UL flame retardant rating		UL 94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.