Material Description

Material Properties:High mobility
Application Areas:Home appliance components
Color:--
Grade:Extrusion grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179	39	kJ/m²
Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	400	J/m
	Impact strength of cantilever beam gap	23°C,6.40mm	ASTM D256	350	J/m
		Impact strength of cantilever beam gap	-30°C	ISO 180/1A	26	kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	37	kJ/m²
Charpy Notched Impact Strength	-30°C	ISO 179	28	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	--6	ISO 178	61.0	Mpa
bending strength	bending strength	--5	ASTM D790	60.7	Mpa
Bending modulus	--6	ISO 178	1700	Mpa
Bending modulus	Bending modulus	--5	ASTM D790	2070	Mpa
elongation	Break	ISO 527-2/50	25	%
elongation	elongation	Break4	ASTM D638	40	%
tensile strength	Break	ISO 527-2/50	30.0	Mpa
	tensile strength	Yield	ISO 527-2/50	41.0	Mpa
	tensile strength	tensile strength	Yield4	ASTM D638	38.1	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	85.0	°C
Vicat softening temperature	--	ASTM D15257	103	°C
Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	99.0	°C
	Hot deformation temperature	1.8MPa,Annealed	ASTM D648	95.0	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	83.0	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	9.1E-05	cm/cm/°C
Vicat softening temperature	--	ISO 306/B50	101	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/A50	106	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate		ISO 294-4	0.40-0.70	%
Melt Volume Flow Rate (MVR)	220°C/10.0kg	ISO 1133	2.50	cm3/10min
melt mass-flow rate	200°C/5.0kg	ASTM D1238	0.50	g/10min
density	23°C	ISO 1183	1.04	g/cm³
density	density	--3	ASTM D792	1.03	g/cm³
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	102

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.