ASA/PC GELOY™ HRA222F WH5D169 SABIC INNOVATIVE SAUDI
304
- Unit Price:US$ 2,854 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:30MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High temperature resistance｜Thermal stability
- Application Areas:Home appliance components｜Lawn garden equipment
- Color:--
- Grade:Injection grade
Technical Data Sheet
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed, 4.00 mm, 100 mm Span | ISO 75-2/Be | 99.0 °C |
| 1.8 MPa, Unannealed, 4.00 mm, 100 mm Span | ISO 75-2/Ae | 88.0 °C | |
| Vicat softening temperature | -- | ISO 306/A50 | 111 °C |
| -- | ISO 306/B50 | 102 °C | |
| -- | ISO 306/B120 | 104 °C | |
| Ball Pressure Test | 73 to 77°C | IEC 60695-10-2 | 通过 |
| Linear coefficient of thermal expansion | Flow : -30 to 80°C | ISO 11359-2 | 6.9E-5 cm/cm/°C |
| Across Flow : -30 to 80°C | ISO 11359-2 | 7.1E-5 cm/cm/°C | |
| Across Flow : 23 to 80°C | ISO 11359-2 | 7.5E-5 cm/cm/°C | |
| RTI Elec | UL 746 | 90.0 °C | |
| RTI Imp | UL 746 | 90.0 °C | |
| RTI | UL 746 | 90.0 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 2.0 mm | UL 94 | V-0 |
| Extreme Oxygen Index | ISO 4589-2 | 29 % |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt Volume Flow Rate (MVR) | 260°C/2.16 kg | ISO 1133 | 13.0 cm3/10min |
| Shrinkage rate | Flow | Internal Method | 0.40 - 0.60 % |
| Water absorption rate | Saturation, 23°C | ISO 62 | 0.60 % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.20 % | |
| Outdoor applicability | UL 746C | f1 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Compared to the anti leakage trace index | UL 746 | PLC 0 | |
| IEC 60112 | V |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 80 to 90 °C | ||
| drying time | 2.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Hopper temperature | 60 to 80 °C | ||
| Temperature at the rear of the barrel | 200 to 230 °C | ||
| Temperature in the middle of the barrel | 220 to 260 °C | ||
| Temperature at the front of the material cylinder | 230 to 270 °C | ||
| Spray nozzle temperature | 220 to 260 °C | ||
| Processing (melt) temperature | 230 to 270 °C | ||
| Mold temperature | 50 to 70 °C |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | --3 | ASTM D638 | 2590 Mpa |
| -- | ISO 527-2/1 | 2520 Mpa | |
| tensile strength | Yield4 | ASTM D638 | 63.0 Mpa |
| Yield5 | ASTM D638 | 59.0 Mpa | |
| Yield | ISO 527-2/5 | 62.0 Mpa | |
| Yield | ISO 527-2/50 | 60.0 Mpa | |
| Break5 | ASTM D638 | 66.0 Mpa | |
| Break4 | ASTM D638 | 56.0 Mpa | |
| Break | ISO 527-2/5 | 51.0 Mpa | |
| Break | ISO 527-2/50 | 45.0 Mpa | |
| elongation | Yield5 | ASTM D638 | 4.2 % |
| Yield4 | ASTM D638 | 4.3 % | |
| Yield | ISO 527-2/5 | 4.3 % | |
| Yield | ISO 527-2/50 | 4.4 % | |
| Break5 | ASTM D638 | > 100 % | |
| Break4 | ASTM D638 | > 100 % | |
| Break | ISO 527-2/5 | > 50 % | |
| Bending modulus | ISO 178 | 2510 Mpa | |
| bending strength | ISO 178 | 93.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.