PPO NORYL GTX™ GTX918WR-50001 SABIC INNOVATIVE JAPAN
3
- Unit Price:US$ 3,830 /MT
- Packaging Specification:
- Supply Quantity:20MT
- Delivery Terms:DDP
- :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility｜High temperature resistance
- Application Areas:Automotive components｜Vehicle electronics｜Parts under the hood of a car
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 45 g/10 min | |
| Melt volume flow rate | ISO 1133 | 5.00 cm3/10min | |
| Shrinkage rate | 内部方法 | 1.3 - 1.6 % | |
| 内部方法 | 1.0 - 1.3 % | ||
| Water absorption rate | ASTM D570 | 4.2 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 810 Mpa | |
| tensile strength | ASTM D638 | 62.0 Mpa | |
| ISO 527-2/50 | 60.0 Mpa | ||
| ASTM D638 | 57.0 Mpa | ||
| ISO 527-2/50 | 55.0 Mpa | ||
| elongation | ASTM D638 | 11 % | |
| ISO 527-2/50 | 4.5 % | ||
| ASTM D638 | 53 % | ||
| ISO 527-2/50 | 30 % | ||
| Flexural modulus | ASTM D790 | 2360 Mpa | |
| ISO 178 | 2200 Mpa | ||
| bending strength | ISO 178 | 85.0 Mpa | |
| ASTM D790 | 98.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 10 kJ/m² | |
| ISO 179/1eA | 20 kJ/m² | ||
| Dart impact | ASTM D3763 | 40.0 J |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 95 to 105 °C | ||
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.070 % | ||
| Suggested injection volume | 30 to 50 % | ||
| Temperature at the rear of the barrel | 255 to 295 °C | ||
| Temperature in the middle of the barrel | 260 to 295 °C | ||
| Temperature at the front of the material cylinder | 265 to 295 °C | ||
| Spray nozzle temperature | 270 to 295 °C | ||
| Processing (melt) temperature | 270 to 295 °C | ||
| Temperature | 65 to 95 °C | ||
| Back pressure | 0.300 to 1.40 Mpa | ||
| screw speed | 20 to 100 rpm | ||
| Exhaust hole depth | 0.013 to 0.038 mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 188 °C | |
| ISO 75-2/Be | 185 °C | ||
| ASTM D648 | 148 °C | ||
| vicat | ASTM D152510 | 242 °C | |
| ISO 306/A50 | 245 °C | ||
| ISO 306/B50 | 190 °C | ||
| ISO 306/B120 | 195 °C | ||
| Linear coefficient of thermal expansion | ASTM E831 | 6.5E-5 cm/cm/°C | |
| ISO 11359-2 | 8.0E-5 cm/cm/°C | ||
| ASTM E831 | 6.8E-5 cm/cm/°C | ||
| ISO 11359-2 | 8.0E-5 cm/cm/°C | ||
| thermal conductivity | ASTM C177 | 0.25 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.