Material Description

Material Properties:Low temperature resistance｜transparent｜Processability｜Moderate liquidity｜Ductility｜copolymer
Application Areas:Electrical field｜Electronic field｜Household appliances｜Household appliances｜Bottle cap
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
transmissivity	2540 μm	ASTM D1003	82.0 %
turbidity	2540 μm	ASTM D1003	3.0 %

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Charpy Notched Impact Strength	23°C	ISO 179/1eA	70 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	60 kJ/m²
Dart impact	-30°C, Total Energy	ASTM D3763	77.0 J
Dart impact	Dart impact	23°C, Total Energy	ASTM D3763	75.0 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.8 mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	V-2
Burning wire flammability index	3.0 mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	0.8 mm	IEC 60695-2-13	850 °C
Hot filament ignition temperature	Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	850 °C

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Yield, 50.0 mm Span4	ASTM D790	92.0 Mpa
bending strength	bending strength	--5,6	ISO 178	88.0 Mpa
Bending modulus	--5	ISO 178	2120 Mpa
Bending modulus	Bending modulus	50.0 mm Span4	ASTM D790	2180 Mpa
elongation	Break	ISO 527-2/50	110 %
	elongation	Break3	ASTM D638	120 %
		elongation	Yield	ISO 527-2/50	5.4 %
		elongation	elongation	Yield3	ASTM D638	5.6 %
tensile strength	Break	ISO 527-2/50	55.0 Mpa
	tensile strength	Break3	ASTM D638	59.0 Mpa
		tensile strength	Yield	ISO 527-2/50	56.0 Mpa
		tensile strength	tensile strength	Yield3	ASTM D638	57.0 Mpa
Tensile modulus	--	ISO 527-2/1	2300 Mpa
Tensile modulus	Tensile modulus	--2	ASTM D638	2180 Mpa

injection	Test Condition	Test Method	Test Result
Suggested injection volume			40 to 60 %
Temperature at the rear of the barrel			270 to 295 °C
Temperature in the middle of the barrel			280 to 305 °C
drying temperature			120 °C
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.020 %
Temperature at the front of the material cylinder			295 to 315 °C
Spray nozzle temperature			290 to 310 °C
Processing (melt) temperature			295 to 315 °C
Mold temperature			70 to 95 °C
Back pressure			0.300 to 0.700 Mpa
Screw speed			40 to 70 rpm
Exhaust hole depth			0.025 to 0.076 mm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	120 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9	ISO 75-2/Af	116 °C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : -40 to 95°C	ASTM E831	6.7E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Flow : 23 to 80°C	ISO 11359-2	6.7E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Across Flow : -40 to 95°C	ASTM E831	8.0E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 80°C	ISO 11359-2	8.0E-5 cm/cm/°C
RTI Elec		UL 746	130 °C
RTI		UL 746	130 °C
Vicat softening temperature	--	ASTM D152510	138 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	139 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.090 %
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	0.12 %
Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.40 - 0.80 %
Shrinkage rate	Shrinkage rate	Flow : 3.20 mm	Internal Method	0.40 - 0.80 %
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	9.00 cm3/10min
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	10 g/10 min

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		ASTM D257	> 1.0E+15 ohms
Volume resistivity		ASTM D257	> 1.0E+15 ohms·cm

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	L -Sale	ISO 2039-2	87

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC LEXAN™ EXL1414T BK16384 SABIC INNOVATIVE SHANGHAI

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet