PA46 Stanyl® TW200F6 9C1900 DSM JAPAN

243

Unit Price:US$ 5,851 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
45MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜wear resistant
Application Areas:Automotive Applications｜Electrical applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	11 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	12 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	65 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	80 kJ/m²
Impact strength of cantilever beam gap	-40°C	ISO 180/1A	11 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	12 kJ/m²

flammability	Test Condition	Test Method	Test Result
Flammability level		UL 94	HB
Flammability level	Flammability level		UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	--	ISO 527-2	10000 Mpa
	Tensile modulus	120°C	ISO 527-2	5500 Mpa
		Tensile modulus	160°C	ISO 527-2	5000 Mpa
			Tensile modulus	180°C	ISO 527-2	4400 Mpa
			Tensile modulus	Tensile modulus	200°C	ISO 527-2	4000 Mpa
tensile strength	Break	ISO 527-2	210 Mpa
	tensile strength	Break, 120°C	ISO 527-2	110 Mpa
		tensile strength	Break, 160°C	ISO 527-2	100 Mpa
			tensile strength	Break, 180°C	ISO 527-2	95.0 Mpa
			tensile strength	tensile strength	Break, 200°C	ISO 527-2	90.0 Mpa
Tensile strain	Break	ISO 527-2	4.0 %
	Tensile strain	Break, 120°C	ISO 527-2	7.5 %
		Tensile strain	Break, 160°C	ISO 527-2	7.5 %
			Tensile strain	Break, 180°C	ISO 527-2	7.5 %
			Tensile strain	Tensile strain	Break, 200°C	ISO 527-2	7.5 %
Bending modulus	--	ISO 178	9000 Mpa
	Bending modulus	120°C	ISO 178	4700 Mpa
	Bending modulus	Bending modulus	160°C	ISO 178	3900 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	290 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	290 °C
Melting temperature		ISO 11357-3	295 °C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	2.5E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	6.0E-5 cm/cm/°C
RTI Elec	0.9 mm	UL 746	140 °C
Thermal Index - 5000 hr		IEC 60216	177 °C

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	1.41 g/cm³
Shrinkage rate	横向Flow	ISO 294-4	1.3 %
Shrinkage rate	Shrinkage rate	Flow	ISO 294-4	0.50 %
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	2.6 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		IEC 60093	1.0E+14 ohms·cm
Dielectric strength		IEC 60243-1	30 KV/mm
Relative permittivity	100 Hz	IEC 60250	4.30
Relative permittivity	Relative permittivity	1 MHz	IEC 60250	4.00
Compared to the anti leakage trace index		IEC 60112	PLC 2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA46 Stanyl® TW200F6 9C1900 DSM JAPAN

Material Description

Technical Data Sheet Compare

Technical Data Sheet