PC/PBT XENOY™ ENH2900-WH9G637 SABIC INNOVATIVE SHANGHAI

307

Unit Price:US$ 2,920 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
98MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Chemical resistance｜Low temperature impact resistance
Application Areas:Household daily necessities｜Electrical applications｜Automotive Applications
Color:--
Grade:Halogen-free flame retardant grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C, Total Energy	ASTM D3763	65.0 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	2.5 mm	UL 94	5VB
	UL flame retardant rating	1.5 mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	1.1 mm	UL 94	V-1

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Yield, 50.0 mm Span	ASTM D790	89.0 Mpa
Bending modulus	50.0 mm Span	ASTM D790	2240 Mpa
elongation	Break	ASTM D638	65 %
elongation	elongation	Yield	ASTM D638	4.0 %
tensile strength	Break	ASTM D638	42.0 Mpa
tensile strength	tensile strength	Yield	ASTM D638	63.0 Mpa
Tensile modulus		ASTM D638	2480 Mpa

injection	Test Condition	Test Method	Test Result
Mold temperature			60 to 80 °C
Processing (melt) temperature			245 to 275 °C
Spray nozzle temperature			245 to 275 °C
Temperature at the front of the material cylinder			245 to 275 °C
Temperature in the middle of the barrel			220 to 265 °C
Temperature at the rear of the barrel			220 to 255 °C
Suggested injection volume			30 to 80 %
Suggested maximum moisture content			0.040 %
drying time			3.0 to 4.0 hr
drying temperature			80 to 90 °C
Back pressure			0.300 to 0.700 Mpa
Screw speed			40 to 70 rpm
Exhaust hole depth			0.038 to 0.076 mm

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature		ASTM D15255	102 °C
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	78.0 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.80 %
melt mass-flow rate	266°C/5.0 kg	ASTM D1238	26 g/10 min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC/PBT XENOY™ ENH2900-WH9G637 SABIC INNOVATIVE SHANGHAI

Material Description

Technical Data Sheet Compare

Technical Data Sheet