Material Description
- Material Properties:Excellent appearance｜Glass fiber reinforced
- Application Areas:Electrical appliances｜Construction field｜Lighting applications｜Plastic bag｜Medical supplies｜Electronic field｜Electrical field
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R 级 | ASTM D785 | 119 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 204 °C |
| 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 187 °C | |
| Linear coefficient of thermal expansion | -40 到 40°C，流动 | ASTM E831 | 4.0E-5 cm/cm/°C |
| 60 到 138°C，流动 | ASTM E831 | 6.1E-5 cm/cm/°C | |
| RTI Elec | UL 746 | 125 °C | |
| RTI Imp | UL 746 | 110 °C | |
| RTI | UL 746 | 125 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | V-0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 350 J/m |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Specific volume | ASTM D792 | 0.650 cm³/g | |
| melt mass-flow rate | 266°C/5.0 kg | ASTM D1238 | 79 g/10 min |
| shrinkage rate | 流动 : 1.50 到 3.20 mm | 内部方法 | 0.40 - 0.60 % |
| 流动 : 3.20 到 4.60 mm | 内部方法 | 0.60 - 0.90 % | |
| 横向流动 : 1.50 到 3.20 mm | 内部方法 | 0.50 - 0.80 % | |
| 横向流动 : 3.20 到 4.60 mm | 内部方法 | 0.80 - 1.1 % | |
| Water absorption rate | 24 hr | ASTM D570 | 0.060 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | ASTM D257 | 1.0E+13 ohms·cm | |
| dielectric strength | 1.60 mm, in Oil | ASTM D149 | 24 KV/mm |
| 3.20 mm, in Air | ASTM D149 | 20 KV/mm | |
| dielectric constant | 100 Hz | ASTM D150 | 3.50 |
| 1 MHz | ASTM D150 | 3.30 | |
| Dissipation Factor | 100 Hz | ASTM D150 | 1.0E-3 |
| 1 MHz | ASTM D150 | 0.013 | |
| arc resistance | ASTM D495 | PLC 6 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 3 | |
| High arc combustion index (HAI) | UL 746 | PLC 4 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 4 | |
| Hot wire ignition (HWI) | UL 746 | PLC 0 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 120 °C | ||
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 40 to 80 % | ||
| Temperature at the rear of the barrel | 240 to 255 °C | ||
| Temperature in the middle of the barrel | 245 to 260 °C | ||
| Temperature at the front of the material cylinder | 250 to 265 °C | ||
| Spray nozzle temperature | 245 to 260 °C | ||
| Processing (melt) temperature | 250 to 265 °C | ||
| mold temperature | 65 to 90 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| screw speed | 50 to 80 rpm | ||
| Exhaust hole depth | 0.025 to 0.038 mm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 断裂 | ASTM D638 | 95.0 Mpa |
| flexural modulus | 50.0 mm 跨距 | ASTM D790 | 5000 Mpa |
| bending strength | 断裂, 50.0 mm 跨距 | ASTM D790 | 143 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.