Material Description
- Material Properties:Conductive｜wear resistant
- Application Areas:Bottle cap｜Electronic and electrical components
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8 MPa, 未退火 | ISO 75-2/A | 163 °C |
| Linear coefficient of thermal expansion | 流动 : 23 到 55°C | 内部方法 | 1.0E-5 cm/cm/°C |
| 横向 : 23 到 55°C | 内部方法 | 9.0E-5 cm/cm/°C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 4.5 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.45 g/cm³ | |
| melt mass-flow rate | 190°C/2.16 kg | ISO 1133 | 3.0 g/10 min |
| Melt volume flow rate | 190°C/2.16 kg | ISO 1133 | 2.40 cm3/10min |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 3.0E+2 ohms | |
| volume resistivity | IEC 60093 | 1.0E+3 ohms·cm | |
| Color number | CD3501 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 80 to 90 °C | ||
| drying time | 3.0 to 4.0 hr | ||
| Processing (melt) temperature | 190 to 210 °C | ||
| mold temperature | 60 to 80 °C | ||
| Injection Pressure | 50.0 to 100 Mpa | ||
| screw speed | 100 to 150 rpm | ||
| injection speed | 0 to 3 m/min |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 11700 Mpa | |
| tensile strength | ISO 527-2 | 130 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 1.5 % |
| flexural modulus | ISO 178 | 10000 Mpa | |
| bending strength | ISO 178 | 185 Mpa | |
| coefficient of friction | Dynamic2 | JIS K7218 | 0.37 |
| 与钢 - 动态3 | JIS K7218 | 0.27 | |
| Wear factor | 0.49 MPa, 0.30 m/sec4 | JIS K7218 | 10 10^-8 mm³/N·m |
| 0.060 MPa, 0.15 m/sec5 | JIS K7218 | 200 10^-8 mm³/N·m | |
| 0.49 MPa, 0.30 m/sec6 | JIS K7218 | 500 10^-8 mm³/N·m | |
| 0.060 MPa, 0.15 m/sec7 | JIS K7218 | 10000 10^-8 mm³/N·m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.