Material Description

Material Properties:High rigidity｜Thermal stability
Application Areas:Automotive Applications｜Engineering accessories
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	100	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Flammability level		UL 94	HB
Polymer Abbreviation			PA6T/6-GF35
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile creep modulus	1000 hr	ISO 899-1	--	Mpa
Tensile strain	Break	ISO 527-2	3.0	%
tensile strength	Break	ISO 527-2	210	Mpa
Tensile modulus		ISO 527-2	12000	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			110	°C
drying time			8.0	hr
Suggested maximum moisture content			0.15	%
Hopper temperature			80	°C
Temperature at the rear of the barrel			300	°C
Temperature in the middle of the barrel			310	°C
Temperature at the front of the material cylinder			320	°C
Spray nozzle temperature			320	°C
Processing (melt) temperature			310 to 330	°C
Mold temperature			80 to 120	°C
Residence Time			< 5.0	min
Screw speed			< 18	m/min
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Maximum operating temperature	短周期操作		270	°C
Temperature index - at 50% loss of tensile strength	--6	IEC 60216	135	°C
Temperature index - at 50% loss of tensile strength	Temperature index - at 50% loss of tensile strength	--5	IEC 60216	160	°C
thermal conductivity		DIN 52612	0.28	W/m/K
specific heat			1300	J/kg/°C
Linear coefficient of thermal expansion	Across Flow : 23 to 55°C	ISO 11359-2	5.0E-5 到 6.0E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow : 23 to 55°C	ISO 11359-2	1.5E-5	cm/cm/°C
Melting temperature		ISO 11357-3	295	°C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	245	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Mold Shrinkage - Constrained			0.35	%
Stickiness	96% H2SO4	ISO 307	130	cm³/g
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.80 to 1.2	%
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	4.3 to 5.3	%
Shrinkage rate	Flow	ISO 294-4	0.30	%
Shrinkage rate	Shrinkage rate	横向Flow	ISO 294-4	1.0	%
Apparent density			0.70	g/cm³
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Relative permittivity	1 MHz	IEC 60250	4.20
Dielectric strength		IEC 60243-1	33	KV/mm
Volume resistivity		IEC 60093	1.0E+15	ohms·cm
Surface resistivity		IEC 60093	--	ohms
Dissipation factor	1 MHz	IEC 60250	0.020

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Dongguan Guangyan	US$ 5970 /MT
Shanghai Huibao/Huibai	US$ 9070 /MT

Supplier Join

Get App

Top

PA6T Ultramid® TKR4355G7 BASF GERMANY

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index