ABS CYCOLAC™  MG47F-NA1000 SABIC INNOVATIVE US

315
  • Unit Price:US$ 1,919 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    10MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View

For more details, please contact the supplier!

Material Description

  • Material Properties:High impact resistance
  • Application Areas:Electronic field｜Automotive sector
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

Filling analysisTest ConditionTest MethodTest Result
Melt viscosity240°C, 1000 sec^-1ASTM D3835225 Pa·s
impact performanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength-30°CISO 179/1eA9.0 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA26 kJ/m²
Dart impact23°C, Total EnergyASTM D376330.0 J
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating1.5 mmUL 94HB
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulus--1ASTM D6382270 Mpa
Tensile modulus--ISO 527-2/12370 Mpa
tensile strengthYield2ASTM D63844.0 Mpa
tensile strengthYieldISO 527-2/5047.0 Mpa
tensile strengthBreak2ASTM D63833.0 Mpa
tensile strengthBreakISO 527-2/5035.0 Mpa
elongationYield2ASTM D6382.0 %
elongationYieldISO 527-2/502.6 %
elongationBreak2ASTM D63824 %
elongationBreakISO 527-2/5025 %
Bending modulus50.0 mm Span3ASTM D7902300 Mpa
Bending modulus--4ISO 1782200 Mpa
bending strength--4,5ISO 17870.0 Mpa
bending strengthYield, 50.0 mm Span3ASTM D79070.0 Mpa
injectionTest ConditionTest MethodTest Result
drying temperature80 to 95 °C
drying time2.0 to 4.0 hr
Suggested maximum moisture content0.10 %
Suggested injection volume50 to 70 %
Temperature at the rear of the barrel190 to 210 °C
Temperature in the middle of the barrel205 to 225 °C
Temperature at the front of the material cylinder215 to 240 °C
Spray nozzle temperature220 to 260 °C
Processing (melt) temperature220 to 260 °C
Mold temperature50 to 70 °C
Back pressure0.300 to 0.700 Mpa
Screw speed30 to 60 rpm
Exhaust hole depth0.038 to 0.051 mm
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature0.45 MPa, Unannealed, 3.20 mmASTM D64894.0 °C
Hot deformation temperature1.8 MPa, Unannealed, 3.20 mmASTM D64880.0 °C
Hot deformation temperature1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span7ISO 75-2/Af81.0 °C
Vicat softening temperature--ASTM D1525899.0 °C
Vicat softening temperature--ISO 306/B5098.0 °C
Vicat softening temperature--ISO 306/B120100 °C
Linear coefficient of thermal expansionFlow : -40 to 40°CASTM E8318.8E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -40 to 40°CASTM E8318.8E-5 cm/cm/°C
RTI ElecUL 74660.0 °C
RTI ImpUL 74660.0 °C
RTIUL 74660.0 °C
Physical propertiesTest ConditionTest MethodTest Result
melt mass-flow rate230°C/3.8 kgASTM D12385.6 g/10 min
melt mass-flow rate220°C/10.0 kgISO 113318 g/10 min
Shrinkage rate3.20 mm，FlowInternal Method0.50 - 0.80 %
Electrical performanceTest ConditionTest MethodTest Result
Arc resistanceASTM D495PLC 6
Compared to the anti leakage trace indexUL 746PLC 0
High arc combustion indexUL 746PLC 0
High voltage arc tracing rateUL 746PLC 3
Hot wire ignitionUL 746PLC 3
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessR-ScaleASTM D785112
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.