Material Description
- Material Properties:Flame retardant｜Filler: Glass fiber reinforced material｜15% filler by weight
- Application Areas:Electrical components｜Electrical appliances
- Color:--
- Grade:Enhanced level
Material Certification
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M计秤,23°C | ISO 2039-2 | 85 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD：-30到100°C | ISO 11359-2 | 5.3E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 220 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 200 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.40mm | UL 94 | V-0 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| BarFlowLength | 250°C,1.00mm | 内部方法 | 150 mm |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | IEC 60093 | 5E+16 ohms·cm | |
| dielectric strength | IEC 60243-1 | 14 KV/mm | |
| dielectric constant | 23°C,50Hz | IEC 60250 | 3.60 |
| 23°C,1kHz | IEC 60250 | 3.80 | |
| Dissipation Factor | 23°C,50Hz | IEC 60250 | 2E-03 |
| 23°C,1MHz | IEC 60250 | 0.020 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 3 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | TD:3.00mm2 | 内部方法 | 1.3 % |
| MD:3.00mm4 | 内部方法 | 0.50 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.070 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 屈服,23°C | ISO 527-2 | 100 Mpa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 2.0 % |
| flexural modulus | 23°C | ISO 178 | 6600 Mpa |
| bending strength | 23°C | ISO 178 | 160 Mpa |
| coefficient of friction | 0.20 | ||
| Friction coefficient - vs. Metal | SuzukiMethod | 0.15 | |
| Tensile modulus | 23°C | ISO 527-2 | 7100 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.