PC LUPOY® 1201-05 LG CHEM KOREA

287

Unit Price:US$ 2,630 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20.5MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:transparent｜wear resistant｜Low viscosity
Application Areas:Toy｜Food containers｜chip｜bottle
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
Refractive index		ASTM D542	1.586
transmissivity		ASTM D1003	89.0	%
turbidity		ASTM D1003	0.70 to 1.5	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C, 3.18 mm, Total Energy	ASTM D3763	94.0	J
Suspended wall beam without notch impact strength	23°C	ASTM D256	无断裂
Impact strength of cantilever beam gap	23°C, 3.18 mm	ASTM D256	950	J/m
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	3.0 mm	UL 94	HB
	UL flame retardant rating	0.50 mm	UL 94	V-2
		UL flame retardant rating	1.6 mm	UL 94	V-2
		UL flame retardant rating	UL flame retardant rating	2.527mm	UL 94	V-2
Hot filament ignition temperature	2.0 mm, 5.0 sec	IEC 60695-2-13	850	°C
Extreme Oxygen Index		ASTM D2863	26	%
Average degree of combustion		ASTM D635	3	CM
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Wear resistance	Delta Haze	ASTM D1004	45	%
bending strength		ASTM D790	96.0	Mpa
Bending modulus		ASTM D790	2410	Mpa
elongation	Break	ASTM D638	150	%
elongation	elongation	Yield	ASTM D638	6.0	%
tensile strength	Break	ASTM D638	72.0	Mpa
tensile strength	tensile strength	Yield, 23°C3	ASTM D638	60.0	Mpa
Tensile modulus		ASTM D638	2410	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa, Annealed, 4.00 mm	ASTM D648	143	°C
	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm	ASTM D648	132	°C
	Hot deformation temperature	Hot deformation temperature	0.45 MPa, Annealed, 4.00 mm	ASTM D648	146	°C
Linear coefficient of thermal expansion	-40 to 82°C，Flow	ASTM D696	6.8E-5	cm/cm/°C
Ball pressure temperature		IEC 60598-1	> 125	°C
Vicat softening temperature		ASTM D15257	151	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium, 23°C, 50% RH	ASTM D570	0.32	%
Water absorption rate	Water absorption rate	24 hr, 23°C	ASTM D570	0.15	%
Shrinkage rate	Flow	ASTM D955	0.50 - 0.70	%
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	5.0	g/10 min
density		ASTM D792	1.20	g/cm³
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity	23°C	ASTM D257	2.0E+17	ohms·cm
Dielectric strength		ASTM D149	17	KV/mm
Dielectric constant	60 Hz	ASTM D150	3.00
Dissipation factor	60 Hz	ASTM D150	1.0E-3
Compared to the anti leakage trace index	2.00 mm	IEC 60112	PLC 2
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	118
Rockwell hardness	Rockwell hardness	M-Scale	ASTM D785	74

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PC LUPOY® 1201-05 LG CHEM KOREA

Material Description

Material Certification

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials