PPA/F/PTFE LNP™ LUBRICOMP™ UFL-4036HS BK8115 SABIC INNOVATIVE US

380

Unit Price:US$ 6,490 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜Flame retardant
Application Areas:tubing｜Lighting applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Multi axis Instrumented Impact Energy		ISO 6603-2	2.00	J
Impact strength of cantilever beam gap	23°C	ISO 180/1A	9.1	kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	47	kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	8.90	J
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Yield	ISO 527-2/5	192	Mpa
	tensile strength	Break	ASTM D638	189	Mpa
	tensile strength	tensile strength	Break	ISO 527-2/5	192	Mpa
elongation	Yield	ASTM D638	1.8	%
Tensile strain	Yield	ISO 527-2/5	2.0	%
elongation	Break	ASTM D638	1.7	%
Tensile strain	Break	ISO 527-2/5	2.0	%
Bending modulus	50.0mmSpan	ASTM D790	10600	Mpa
Bending modulus	Bending modulus		ISO 178	11300	Mpa
bending strength	Yield,50.0mmSpan	ASTM D790	242	Mpa
Tensile modulus	--2	ASTM D638	15400	Mpa
	Tensile modulus	--3	ASTM D638	15400	Mpa
	Tensile modulus	Tensile modulus		ISO 527-2/1	12600	Mpa
tensile strength	Yield	ASTM D638	189	Mpa
bending strength	Break,50.0mmSpan	ASTM D790	233	Mpa
Friction coefficient	Dynamic	ASTM D3702Modified	0.48
Friction coefficient	Friction coefficient	Static	ASTM D3702Modified	0.52
Wear factor	Ring	ASTM D3702Modified	0.100	10^-10in^5-min/ft-lb-hr
Wear factor	Wear factor	Washer	ASTM D3702Modified	5.00	10^-10in^5-min/ft-lb-hr
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	277	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	273	°C
Linear coefficient of thermal expansion	MD：-30to30°C	ASTM D696	2.1E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-30to30°C	ASTM D696	4.5E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	MD：24hr	ASTM D955	0.20-0.40	%
Shrinkage rate	Shrinkage rate	TD：24hr	ASTM D955	0.80-1.0	%
Water absorption rate	24hr,50%RH	ASTM D570	0.15	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.25	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Tenamo (Guangdong)	US$ 6490 /MT

Supplier Join

Get App

Top

PPA/F/PTFE LNP™ LUBRICOMP™ UFL-4036HS BK8115 SABIC INNOVATIVE US

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index